Electronics Forum | Tue Oct 06 07:37:01 EDT 2015 | m_imtiaz
can we use same reflow oven for lead free and leaded solder paste, is there any chance of lead contamination in lead-free products.
Electronics Forum | Wed Oct 07 13:15:06 EDT 2015 | markhoch
You can most certainly use the same reflow oven for both leaded and lead-free pastes. Obviously your thermal profiles will be different, as the lead-free paste should have a higher reflow temp. As long as your oven has adequate exhaust and flux manag
Electronics Forum | Tue Jan 20 10:00:25 EST 2015 | TM
Hello We are currently cleaning stencils from both process (PbSn and lead free) in the same cleaning machine. A customer is concerned about cross contamination of lead between stencils. Is there any test kit or tool that you can suggest to test the
Electronics Forum | Tue Jan 20 16:26:59 EST 2015 | emeto
There are a lot of lead testers out there. Just google it. I personally don't think you will find anything wrong, but for the pleasure of your customers buy one and prove it. I would also check the lead on the squeegees of your stencil printers and t
Electronics Forum | Mon Nov 11 10:51:40 EST 2013 | dyoungquist
Are you using lead or lead-free solder? 260C would be good for lead solder but may be a bit low for lead-free. We run our lead-free selective solder pot at 300C although we do not have any pre-heat or top heat, just hot nitrogen blowing around the
Electronics Forum | Mon Nov 11 10:54:05 EST 2013 | mleber
We are leaded only. (Military CM)
Electronics Forum | Fri Apr 16 11:03:35 EDT 2004 | davef
Your copper corrosion is not good. It indicates that you have not done a good job in cleaning. [We assume this is a medium green color, not unlike the color of the solder mask on your board, that is almost like a translucent lacquer; rather than th
Electronics Forum | Mon Aug 09 20:47:21 EDT 2004 | KEN
I think OA flux left on the pot would quickly looses its activity and become part of the dross waste stream, and smoke stream for that matter. Also, if your wave is setup properly your selective pallets will scour (push) the top of the lambda wav
Electronics Forum | Thu Dec 04 10:26:06 EST 2008 | billmeye
Is anyone aware of any white papers regarding the possibility of lead contamination on ROHS assemblies from using the same test fixture with the same test probes on both tin/lead and ROHS assemblies. We have customers switching over but we are still