Electronics Forum | Thu Nov 30 20:41:35 EST 2000 | Roland
Larry, SMTnet.com did an Onboard Forum regarding lead free solder. The link : http://www.smtnet.com/onboard/get_forum.cfm?session_id=4& Also, I did a search of the SMTnet forum (left side of most pages-please be patient it takes a moment) using th
Electronics Forum | Wed Feb 20 23:17:34 EST 2002 | surachai
I AM JUST EVALUATION LEAD FREE EVALUATION AND FOUND THE BIG PROBLEM OF SOLDER CRACK BETWEEN TERMINAL OF COMPONENT AND THE INTERMETALLIC LAYER OF LEAD FREE ALLOY BUT DON'T FIND ANY CRACK BETWEEN SOLDER AND SURFACE OF PCB , COULD YOU HELP ME VERIFY T
Electronics Forum | Fri Dec 13 16:39:42 EST 2002 | Gris
Hi, Look for papers on SMTA there are a lot of papers on lead free rework. If you dont find any let us know here I am sure you will receive many. Here are a just a few http://www.google.com/search?hl=en&ie=UTF-8&oe=UTF-8&q=%22lead+free+rework%22&
Electronics Forum | Fri Feb 22 15:16:24 EST 2002 | rkevin
Bet your using tin/ lead plated components with a lead free Cu/Ag/Sn alloy. It leads to intermetallic cracking. Wow didn't anyone tell you to check the archives yet, It seems to be the answer given to everyone. Why have an interactive site if you alw
Electronics Forum | Thu Oct 01 09:58:30 EDT 1998 | Jacqueline Coia
Could you tell me please when the lead free solder regulation will become mandatory in Europe and also what are the current industrial alternatives for paste, bar and wire. Cheers, Jack
Electronics Forum | Wed Oct 07 15:44:43 EDT 1998 | CW
There's a good article on lead-free assembly of mixed technology in the May issue of SMT Magazine (pg. 52)
Electronics Forum | Thu Feb 16 12:41:50 EST 2006 | fredericksr
Hey folks, I was interested in any information that you might have on tombstone reduction when using a lead free solder and profile. Thanks for any input that you may have! -Russ #x
Electronics Forum | Wed Jan 28 21:47:56 EST 2009 | padawanlinuxero
Hello! I am having trouble with the new changes from lead joint to lead free joint, we are working on change to lead free, I am using a 3 zone oven reflow, the zone temps are : zone 1 zone 2 zone 3 (top and bottom) 128 208 260 th
Electronics Forum | Tue Oct 21 23:28:59 EDT 2003 | xz xiao
We all know the Lead Free process is trend, so we trial run it, now it is only my comment that we have a good achievement after several tries,we have taken serveral photos about Lead Free process with ErsaScope. 1.The surface of the solder joint are