Electronics Forum | Tue Dec 09 19:04:54 EST 2008 | gregoryyork
you need to check your angle on this, can you measure and advise what you have cheers Greg York
Electronics Forum | Wed Dec 10 01:56:12 EST 2008 | lococost
The angle is a standard Soltec 7deg. We don't have the tools to measure this accuratly, but I do trust Soltec on this.
Electronics Forum | Tue Oct 18 19:34:02 EDT 2011 | warwolf
so there is no one here baised in New Zealand that wants to buy our SAC305 solder dross and recycle it, we have about 120KG at the moment, anyone intrested?
Electronics Forum | Fri Jun 11 13:20:32 EDT 2004 | raylawre
We have segregation of materials, Different storage areas for paste and Bar stock, etc. We are bar coding the solder paste materials (have to scan paste container, and blades before use, etc. line won't run unless its good). Also changed packaging s
Electronics Forum | Sat Jun 12 19:08:11 EDT 2004 | Ken
Well, it finally happened. A machine Operator did not follow our bar code process and "grabbed a tube of solder paste" and guess what. Built 250 assemblies with LF paste when it should have been Tin/Lead!!!! SOLDER PASTE SUPPLIERS: can you make t
Electronics Forum | Wed Oct 19 20:04:06 EDT 2011 | warwolf
yeah I’ve tried to go down the road of internal recycling but the company carnt justify spending 20k on a machine that does it. Ah but where still onto it in other places though our SMT department has very minimal wastage on solder paste as we have b
Electronics Forum | Wed Oct 19 11:33:15 EDT 2011 | caerleon
easier if you recycled on-site? You can still send off for reclaimation the oxide powder that your left at the end of the process. Failing that talk to your supplier to see if they have arrangements to do this for you or look at reducing dross - i f
Electronics Forum | Fri Oct 28 21:46:35 EDT 2011 | rdh_41
Hi , I'm interested in Tin and hoping to open long-term business relationship with your company. We are Taiwan-based company dedicate in Tin (Sn). We are looking for opportunity to work with you. And it would be great if you have large quantity of t
Electronics Forum | Wed Jul 06 18:05:57 EDT 2005 | Dave
lead free transition. want to use lead free parts w/ lead solder.. any issues I should be aware of???
Electronics Forum | Wed Jul 06 18:11:37 EDT 2005 | russ
Please search the archives as this has been discussed on many occasions. Everything should be fine except for BGAs which will require a higher temp of 235C at the peak in reflow.