Electronics Forum | Fri Jul 06 12:39:01 EDT 2007 | blnorman
What's the metallization on the board? We use an immersion tin board and had to increase our profile to successfully solder.
Electronics Forum | Wed Aug 12 04:37:14 EDT 2009 | sachu_70
SAC305 has a liquidous state temperature 217 degC. Check the datasheet to compare to this temp. I suppose, it may be lower. - Cheers !
Electronics Forum | Wed Aug 12 14:37:41 EDT 2009 | davef
Try this: http://www.pwbrc.org/members/pdf/works99/Hua.PDF
Electronics Forum | Mon Jul 16 09:53:36 EDT 2007 | ed_faranda
Yes, you can use lead-free parts in a leaded process. And the other is true as well, no-lead free parts in a leaded process. BUT, you should not use leaded parts through a non-lead wave solder process and of course, your board will not be RoSH.
Electronics Forum | Thu May 15 21:52:33 EDT 2008 | deni
Can anyone tell me what makes the wave solder machine lead free? I I am looking to buy a used machine "electrovert minipak 300" and they are claiming that they can convert the machine into lead free. I want to know what does involve to do this kind o
Electronics Forum | Wed Aug 03 21:29:59 EDT 2005 | Ken
Yes, lead can promote fillet lift. In order to understand this defect you must begin looking at your lead frame mateials. some lead frames are more susceptable to this disorder. This is most likely a cte mismatch disorder. Lead contamination in
Electronics Forum | Thu Sep 13 22:06:02 EDT 2007 | davef
While you're waiting for others to respond, here's one take on bismuth in lead-free soldering [ http://smt.pennnet.com/Articles/Article_Display.cfm?Section=Articles⊂section=Display&ARTICLE_ID=229915 ] by a long term friend of SMTnet. Find more by sea
Electronics Forum | Tue Feb 27 12:45:08 EST 2007 | russ
Boy it is good to see the wave master back in action! I mean really guys, is Larry the only one here who knows that the lead turns into vapor in the oven and then in the cooling zones it falls back onto the board and creates the solder joints? P.
Electronics Forum | Thu May 18 16:10:18 EDT 2006 | adlsmt
We did a tin bath on ours but it was provided for free by Nihon Superior so that is a no-brainer. It was better than taking a risk of having to dump the pot. If you cant get a free tin bath, then you should probably go ahead and fill it half way or s
Electronics Forum | Sun Sep 23 18:59:59 EDT 2007 | darby
I presume you are looking at low melting point solders. Firstly, I would consider running BOTH sides with the same paste - this will cut down the opportunities for a mix up with rework or retro-fit. Secondly, check that there is a cored wire availabl