Electronics Forum | Wed Nov 02 11:14:45 EST 2005 | Doug
I am doing lead free testing on a Vitronics selective machine with a 4 mm nozzle. The finishes I am testing are ENIG, ImSn, and ImAg. The problem I am encountering is achieving good top side wetting. Has anyone had any luck with this type of an ap
Electronics Forum | Thu Nov 03 09:43:55 EST 2005 | lupo
Check flux penetration and type of flux. How much is solid contents. The solder filling is better under Nitrogen. Check the time (speed) of the nozzle whether is correct. Usually For SAC305 the temperature of bath is 320C/degrees, but only for sel
Electronics Forum | Fri Jun 23 15:11:11 EDT 2017 | emeto
Try add a pre-heater. If not change the process or the machine. With KISS you will hardly get any PCB to work properly.
Electronics Forum | Sat Jun 24 07:23:06 EDT 2017 | tch
You will need to preheat the boards for a lead free selective solder process. A preheat module is critical for any wave or selective solder process, if you don't get the board preheated properly the solder is going to resist flowing to the top of the
Electronics Forum | Fri Jun 23 12:54:53 EDT 2017 | guts1872
We are having issues with top fill and dropping pins on Molex connectors with our KISS 101. Unfortunately we do not have a pre heater and bottom side pre heat with our nozzles is not satisfactory. Most of the issues occur when using a no clean proces
Electronics Forum | Thu Jun 29 12:07:09 EDT 2017 | georgetruitt
HOW THICK IS THE BOARD? IS THERE A LOT OF COPPER IN THE BOARD? DOES YOUR CUSTOMERS PROVIDE HEAT RELIEF IN THE BOARDS BARREL DESIGN THERE NEEDS TO BE PLENTY OF ROOM FOR LEADFREE SOLDER TO FLOW, DID YOU CHECK YOUR PIN(LEAD)TO HOLE (BARREL) RATIO? N
Electronics Forum | Thu Apr 27 03:23:25 EDT 2006 | ge_lim
According to seho, for multi dipping the process window is very small and they would prefer drag soldering which has a wider window. What is your view on dip vs drag? Why? Other machine user also share the same suggestion?
Electronics Forum | Sun Jul 04 13:27:31 EDT 2021 | dilogic
We are looking for new entry-level selective soldering machine. I would appreciate if you can share experience with the equipment you have, as there are many machines on the market and it's a though choice. We will use it for lead-free soldering and
Electronics Forum | Thu Jun 03 17:43:34 EDT 2004 | g2garyg2
Hi Doug, Read your inquiry. My company PRO-MATION has some exciting technologies available for both top side and bottom side selective laser soldering. Our work cells are great for low volume / high mix environments and are capble for both Tin Lead
Electronics Forum | Thu Jan 22 10:21:46 EST 2015 | charliedci
I am curious to know how others are providing N2 for their lead free selective soldering process. If you are utilizing a nitrogen generator, is it a PSA type or Membrane type? I am trying to get a handle on nitrogen purity and what purity is necessar