Electronics Forum | Tue May 13 07:04:54 EDT 2014 | hemant_pang23
I am looking for the solder wire leaded or lead free which can withstand the solder joint at temperature 450deree Celsius or more after soldering, since i need to form a solder joint at higher temperature area Pls suggest the part number for the sam
Electronics Forum | Tue Aug 21 12:54:45 EDT 2007 | cedams
A long time a go I designed Wave Solder Pallets for lead based solders, but having been out of that industry for a number of years I need to design some new pallets for lead free. We used Titanium to support and mask areas of the board and that work
Electronics Forum | Tue Nov 13 14:11:26 EST 2007 | ratsalad
We use SAC305 for solder paste, and we have been pretty happy with it. When we jumped in to this Pb-free business I was a little nervous due to all the horror stories you hear about the process changes. It's not that big of a deal (at SMT). Over
Electronics Forum | Mon Jun 19 13:56:59 EDT 2006 | netellink
Bolos, Why you have to purchase the Titanium solder pot for your lead-free? I have the MDS-200 Unit Design Drag solder and I just empty the solder SN63PB37 in the solder pot, clean it very well and buy lead-free solder bar to fill up the pot. David
Electronics Forum | Wed May 16 08:26:34 EDT 2007 | davef
It's possible that your lead-free solder will stick to mounting bolts more than SnPb solder. Lead-free solder has a high tin content. Tin is a very good solvent. You may need to coat the bolts with a solder mask to prevent the solder from sticking.
Electronics Forum | Tue Aug 12 15:30:50 EDT 2003 | larryk
With components all switching to lead free, I'm just wondering how many of you in the US have switched to lead free soldering processes? How many of you are playing with lead free and have a plan to implement it into your process? I'm interested in
Electronics Forum | Mon Mar 16 13:35:20 EDT 2015 | swiese242
This has been a challenge for most manufacturers. It depends on board thickness, lead or lead free paste/parts. We have a slim-kic to get the profiles correct in our 14 zone oven. I believe it may be the recently posted suggestion of too much heat in
Electronics Forum | Tue Oct 19 10:10:39 EDT 2004 | Claudine Y. Corda
My company now sells the EVS solder recovery system. Yes, there are companies reclaiming lead-free. Hopefully an actual user will respond to your post but you can feel free to email me if you want me to put you in touch with an end-user. cycorda
Electronics Forum | Sat Nov 12 07:25:26 EST 2005 | GS
In other words it should mean that Lead Free Soldering Process (this SACs era, and not for istance classic Lead Free Sn/In used since many years ago) is still a "Baby Technology" and so we need experience and feedback from the field before to issue
Electronics Forum | Sat Aug 30 12:36:05 EDT 2008 | omid_juve
we are doing many experiment on this problem 1)sn63 pb37 solder paste +normal profile 2)sn62 pb36 ag2 solder paste +normal profile 3)pb free solder paste + pb free profile 4)sn63 pb37 solder paste + pb free profile but still the problem exist so i th