Electronics Forum | Tue Oct 21 23:28:59 EDT 2003 | xz xiao
We all know the Lead Free process is trend, so we trial run it, now it is only my comment that we have a good achievement after several tries,we have taken serveral photos about Lead Free process with ErsaScope. 1.The surface of the solder joint are
Electronics Forum | Wed Nov 02 11:25:46 EST 2005 | dougm
I should specify that I am using SAC 305 as well.
Electronics Forum | Fri Feb 17 11:01:47 EST 2006 | amol_kane
with lead-free solders, one would expect to find less instances of tombstoning. this is because SAC alloys are not eutectic and melt over a range of temp (usually 217-220 deg C) instead of at a single temperature. therefore the forces due to solder s
Electronics Forum | Wed Nov 17 10:03:29 EST 2010 | scottp
Instead of a minimum thickness, we require no exposed copper or SnCu intermetallic. We've been having a lot of trouble lately with suppliers of SN100 HASL boards giving us pads with very irregular solder deposits with areas of exposed intermetallic.
Electronics Forum | Thu Feb 16 12:41:50 EST 2006 | fredericksr
Hey folks, I was interested in any information that you might have on tombstone reduction when using a lead free solder and profile. Thanks for any input that you may have! -Russ #x
Electronics Forum | Mon Jul 30 10:17:26 EDT 2007 | davef
immersion ...easily changes color.. See that's the GREAT thing about immersion coatings. If they change color, they probably will not solder well. Try that with other coatings.
Electronics Forum | Thu Jan 29 16:48:49 EST 2009 | slthomas
Looks like a time/temperature problem to me. However, there are a lot of solder fines surrounding the pads in one photo that go beyond what I'd expect from inadequate TAL. Is it possible that the board was misprinted and not completely cleaned, or
Electronics Forum | Fri Aug 12 13:17:00 EDT 2005 | patrickbruneel
To all smt neters, In many different threads I have tried to bring awareness of the dangers lead free alloys pose to the reliability of solder connections. Many times those warnings have been waved by unscientific reports (from lead free solder manu
Electronics Forum | Wed Nov 02 11:14:45 EST 2005 | Doug
I am doing lead free testing on a Vitronics selective machine with a 4 mm nozzle. The finishes I am testing are ENIG, ImSn, and ImAg. The problem I am encountering is achieving good top side wetting. Has anyone had any luck with this type of an ap
Electronics Forum | Sat Jul 28 08:37:52 EDT 2007 | davef
There is no good choice. Board Finishes: Industrial/Battelle Class 3 Environment [Reliability Knowledge Gaps: For use of Pb-free solders in High Reliability Applications, J Smetana, iNEMI Availability of SnPb-Compatible BGAs Workshop, March 1, 2007,