Electronics Forum | Fri Jan 30 06:28:42 EST 2009 | gregoryyork
Hi Armando Hotflow 7 is a big machine and one of the best Reflow ovens around (in my opinion), well suited for Lead Free. A typical 1.6mm board has the following settings for Lead Free SAC305 paste All Temperature settings are Top and Bottom Prehea
Electronics Forum | Thu Jan 29 16:48:49 EST 2009 | slthomas
Looks like a time/temperature problem to me. However, there are a lot of solder fines surrounding the pads in one photo that go beyond what I'd expect from inadequate TAL. Is it possible that the board was misprinted and not completely cleaned, or
Electronics Forum | Fri Feb 17 11:01:47 EST 2006 | amol_kane
with lead-free solders, one would expect to find less instances of tombstoning. this is because SAC alloys are not eutectic and melt over a range of temp (usually 217-220 deg C) instead of at a single temperature. therefore the forces due to solder s
Electronics Forum | Tue Dec 12 01:52:05 EST 2006 | hemu_me
As we have vitronics oven(SMR610A) made in dec,1997,which has 5 heating zones and 2 cooling zones. For Lead free soldering what should be our baseline for low/medium boards.we have gathered profiles from various paste manufacturers,however we don't k
Electronics Forum | Thu Nov 03 09:43:55 EST 2005 | lupo
Check flux penetration and type of flux. How much is solid contents. The solder filling is better under Nitrogen. Check the time (speed) of the nozzle whether is correct. Usually For SAC305 the temperature of bath is 320C/degrees, but only for sel
Electronics Forum | Thu May 11 18:59:40 EDT 2000 | lboone
Have anyone perform wave soldering on FR-2 and FR-1 printed circuit board with lead free soldering? Can you share the parameters(wave temperature,preheat temperature, contact time, wave height,etc,) used and did you do any changes to the wave solderi
Electronics Forum | Tue Jul 12 06:13:30 EDT 2005 | dougs
A while back we checked out all our manufacturing equipment for lead free capability, we thought our soldering irons would all be fine as they can reach temperatures well in excess of lead free alloy melting points. Last week i was speaking to someo
Electronics Forum | Tue Aug 31 17:36:36 EDT 2004 | davef
NO-LEAD COMPONENTS WITH LEAD SOLDER ISSUE: We agree with Russ. We've dicussed this several times on SMTnet. For instance, look here http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=25394 LEAD COMPONENTS WITH NO-LEAD SOLDER ISSUE: We disa
Electronics Forum | Tue Oct 17 03:13:10 EDT 2006 | charless
Apoligies Steve if I did not explain myself clearly. We have made the same design using the same RoHs compliant components (which I am assured by the suppliers are process temperature capable) with both lead and lead free solder. Without wishing to
Electronics Forum | Tue Aug 15 19:07:13 EDT 2006 | vlad_uk
With the added temperature peak associated to Lead free reflow is anyone seeing or concerned about the increased vapor pressure that may result from moisture entrapment in moisture sensitive components?