Also concider if you will be going lead free in the future as conversion can be a added expense. You may think about learning and going lead free from the begnining as the indestry is rapidly moving in this direction.
Electronics Forum | Fri Nov 27 15:46:28 EST 2009 | jrr3434
Would i be able to use the cast iron pot from my electrovert with out any problems? I thought the tin would dissolve the iron in the pot? This lead free thing is a headache!
Electronics Forum | Mon Nov 15 14:26:11 EST 2004 | nrocco
also the balls need to be lead free, just to make it more interesting.
Electronics Forum | Fri Feb 25 09:30:36 EST 2005 | cisridn
Thanks Pete C I will check them out today.
Electronics Forum | Wed Jun 15 12:23:43 EDT 2005 | patrickbruneel
Hi Russ, Very innovative are you planning on reloading lead-free any time soon?
Electronics Forum | Mon Nov 05 17:17:27 EST 2007 | davef
Radio Shack "Lead-free" Sn96Ag4 480�F
Electronics Forum | Sat Nov 21 11:37:28 EST 2009 | tpappano
Isn't it more like 20 centuries, at least? 8-)
Electronics Forum | Sat Jun 24 07:23:06 EDT 2017 | tch
You will need to preheat the boards for a lead free selective solder process. A preheat module is critical for any wave or selective solder process, if you don't get the board preheated properly the solder is going to resist flowing to the top of the
Electronics Forum | Fri Jun 23 12:54:53 EDT 2017 | guts1872
We are having issues with top fill and dropping pins on Molex connectors with our KISS 101. Unfortunately we do not have a pre heater and bottom side pre heat with our nozzles is not satisfactory. Most of the issues occur when using a no clean proces