Electronics Forum | Thu Apr 15 15:54:13 EDT 2004 | pjc
You ned to speak with an apps engineer from a paste supplier that can go through their alloys. I know Indium has such alloys. Any vendor should be able to supply you a list of alloys avbl in NC paste with their liquidous points.
Electronics Forum | Thu Jul 20 16:28:55 EDT 2000 | Bob Willis
Most robust wave soldering machines will cope with lead free alloys. The temperatures in air that we have run has been between 260-265C. In my opinion the dross generation has not been significantly effected. I was doing a workshop for a well known
Electronics Forum | Wed Apr 14 20:24:48 EDT 2004 | Ken
What do you mean the solder must "survive" 260C? What is your target temperature? Is it dictated by a component, the substrate or the solder alloy? Do you require a eutectic alloy? If not, the selection of alloys grows. (these are from memory...n
Electronics Forum | Thu Apr 15 20:48:57 EDT 2004 | Ken
Tin antimony mp = 236-240C 80Au / 20SN mp = 280C sn25 Ag10 sb = 365C There are very few high temperature service alloys. how about filling a 1400lb pot with 80% Gold! What is the application?
Electronics Forum | Thu Mar 20 09:01:33 EDT 2008 | meritajs
Thanks Greg Our main problem is that we are putting small number PCB through, about300 PCB, size180*250. Such number order our customer in week. In result we got such high solder consumption and high production cost. We will tray to use antiacidant.
Electronics Forum | Fri Mar 21 08:39:38 EDT 2008 | lococost
If you are saying you're going through 1kg/h while only producing 300 pcbs a week and the rest of the time the machine is standing still, then 1.there is something seriously wrong with your machine or 2. check if an operator is suddenly covered in sh
Electronics Forum | Tue Mar 18 05:32:09 EDT 2008 | gregoryyork
What volume of boards are you putting through. 1Kg per hour does sound very high but then again it does depend on volume Using an antioxidant is a must with Lead Free some alloys have additions in them to start with but those drop out with use so th
Electronics Forum | Wed Feb 20 23:17:34 EST 2002 | surachai
I AM JUST EVALUATION LEAD FREE EVALUATION AND FOUND THE BIG PROBLEM OF SOLDER CRACK BETWEEN TERMINAL OF COMPONENT AND THE INTERMETALLIC LAYER OF LEAD FREE ALLOY BUT DON'T FIND ANY CRACK BETWEEN SOLDER AND SURFACE OF PCB , COULD YOU HELP ME VERIFY T
Electronics Forum | Thu Nov 17 13:13:49 EST 2005 | Mike
Hello, Some questions.... Are you running lead free? What alloy? What�s your pot temp at? Temp of the board after preheat? Are you getting any solder in the barrels (
Electronics Forum | Fri Oct 08 08:26:03 EDT 1999 | Carol Zhang
| | | I have a board, 4 spacers needed to be soldered on the board | | | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first, ther
winsouce.jpg)