Electronics Forum | Thu Oct 07 16:57:02 EDT 1999 | Glenn Robertson
| | I have a board, 4 spacers needed to be soldered on the board | | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first, there wi
Electronics Forum | Mon May 16 18:03:30 EDT 2005 | davef
Key Issue: Will this machine solder your boards? You never know until you solder one. Any other avenues of analysis involve substantial risk. Flux Selection * High or low solids * VOC or VOC-free Solder Alloy * If using lead-free, avoid stainles
Electronics Forum | Fri Feb 22 15:16:24 EST 2002 | rkevin
Bet your using tin/ lead plated components with a lead free Cu/Ag/Sn alloy. It leads to intermetallic cracking. Wow didn't anyone tell you to check the archives yet, It seems to be the answer given to everyone. Why have an interactive site if you alw
Electronics Forum | Fri Oct 08 10:08:48 EDT 1999 | Glenn Robertson
| | | | I have a board, 4 spacers needed to be soldered on the board | | | | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first,
Electronics Forum | Thu Sep 08 06:19:55 EDT 2005 | lupo
Hello, Could anyone provide some support concern issue with vertical fill of through hole solder. Our lead free wave soldering process is not capable to fill 100% (requirement of our customer)through hole. We made everything (DoE) - different amoun
Electronics Forum | Sat Nov 21 12:28:00 EST 2009 | flipit
There is evidence of lead being used in soldering 5000 years ago in Mesopotamia. Not a big issue for most people doing SMT but the poster should also understand why percent metal is adjusted for different solder paste alloys. You print by volume b
Electronics Forum | Thu Jul 01 17:35:30 EDT 2004 | Sofia
Hi Everyone, I am just curious, is there a guidline that people follow for choosing their lead-free solder paste? In other words, how do people know whether they should use Indium alloy, or Castin (Sn/Ag/Cu), or whatever else? Thanks
Electronics Forum | Fri Jan 04 15:42:03 EST 2002 | nwyatt
There are several implications: - some lead free alloys do not form an acceptable solder joint when used with lead contaning paste. (ie. Bismuth) - if you use both lead free and lead containing components, you will have different solder joint compos
Electronics Forum | Wed Jun 22 14:14:42 EDT 2005 | Steve
Tin/Lead we have had no problem in masking off areas on a pcb during wave soldering. Lead Free alloys, Nickel Silver Copper would there be any compatability issues with a Peelable latex solder mask containing Ammonia. Really hot need to know.
Electronics Forum | Fri Jul 02 17:05:26 EDT 2004 | blnorman
Depends on your specific application. Can you handle lower reflow temps? Can your parts handle higher reflow temps? What environment will your assembled product have to endure? Lot of different factors come in to play when choosing the right allo