Electronics Forum | Tue Oct 06 07:37:01 EDT 2015 | m_imtiaz
can we use same reflow oven for lead free and leaded solder paste, is there any chance of lead contamination in lead-free products.
Electronics Forum | Wed Oct 07 13:15:06 EDT 2015 | markhoch
You can most certainly use the same reflow oven for both leaded and lead-free pastes. Obviously your thermal profiles will be different, as the lead-free paste should have a higher reflow temp. As long as your oven has adequate exhaust and flux manag
Electronics Forum | Tue Jan 20 10:00:25 EST 2015 | TM
Hello We are currently cleaning stencils from both process (PbSn and lead free) in the same cleaning machine. A customer is concerned about cross contamination of lead between stencils. Is there any test kit or tool that you can suggest to test the
Electronics Forum | Wed Oct 12 11:19:46 EDT 2005 | patrickbruneel
Yeah, adopting is the right word. In this new lead-free era spec.'s are made to stay within the scoop of the RoHS directive. The driving force for spec.'s should be reliability. Did you see any impurity level spec.'s yet in wave soldering for Cu, Au,
Electronics Forum | Tue Feb 08 11:09:44 EST 2005 | jdumont
Hi all, we're preparing for the switch to lead free and I was wondering how dangerous/harmful to our new wave oven it would be to run tin lead parts through the no lead wave. Will the lead build up and cause issues?
Electronics Forum | Fri Oct 14 04:00:05 EDT 2005 | steve
Your friendly wave guy here, check out Aim solders web site. click to the right where it says lead free. There is a complete discussion on what can occur. http://www.aimsolder.com
Electronics Forum | Tue Feb 08 19:10:09 EST 2005 | DasonC
Lead free is not define as NO lead and "a maximum concentration value of 0.1% by weight in homogeneous materials for lead shall be tolerated." Check below link. So replaced your solder from the pot when exceed 0.1%. http://www.leadfree.org/files
Electronics Forum | Mon Aug 09 20:47:21 EDT 2004 | KEN
I think OA flux left on the pot would quickly looses its activity and become part of the dross waste stream, and smoke stream for that matter. Also, if your wave is setup properly your selective pallets will scour (push) the top of the lambda wav
Electronics Forum | Tue Aug 02 22:49:55 EDT 2005 | davef
IPC-A-610D Section 5, shows a variety of photographs of: * Good lead-free solder connections * Lead-free soldering anomalies Hot Tear / Shrink Hole is one such anomaly. This shrinkage effect appears primarily on wave-soldered joints, but can also
Electronics Forum | Thu May 18 14:50:08 EDT 2006 | grantp
Hi, The bath is titanium coated, and the machine is only 2 years old, and was designed for lead free, so we know we don't need to change anything. The reason the supplier gave for suggesting the bath change is "other companies are doing it" and it'