Electronics Forum | Sat Nov 03 10:57:27 EDT 2012 | davef
EricR: Regarding "*** By the way, since we have used the Tin-Silver-Copper lead free solder there has been a strange liquid type chemical leek from the oven exhausted pipes." ... I don't know anything about your process, but the first thing I'd inve
Electronics Forum | Fri Jun 19 14:25:24 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | There has b
Electronics Forum | Mon Apr 09 19:50:33 EDT 2012 | action_101
Hello, We're building some boards with 01005's and the only issue we are running into is the solder is not reflowing. It's the damnest thing, we are having no issues with the printing process or placing the components, the two areas we thought we wo
Electronics Forum | Sat Jun 30 11:03:29 EDT 2001 | davef
Nice to have you back on SMTnet. Some of the newer folk have missed-out on the solid contributions you�ve made to the Forum. The chicken wire cleaning basket was a classic!!! [It�s a shame that the folk at SMTnet can�t recover those files.] We bu
Electronics Forum | Wed Apr 30 14:10:21 EDT 2008 | samir
Doug, yes sir there are some excellent stuff out there in the fine SMTNet archives. Here's one example: http://www.smtnet.com//forums/index.cfm?fuseaction=view_thread&CFApp=1&Thread_ID=9822&#Message39512
Electronics Forum | Thu May 01 21:47:12 EDT 2008 | dphilbrick
Took a couple of jumps to other threads but it was there http://www.mot.co.jp/about/ehs/green/ENV_PBFREEOV.pdf This document was exactly what I needed to send to my paranoid customer! Thanks again!
Electronics Forum | Wed Apr 30 12:26:10 EDT 2008 | dphilbrick
There must be discussions about this on SMTnet but I have yet to find them. I would like to hear from all you smart people about running LF and PB BGA�s on the same board using 63/37 solder. If you run your profile up to peak at around 225C +/- (nitr
Electronics Forum | Tue Jan 31 10:59:55 EST 2006 | carterhoward
Hi All, I�ve been doing some research on the issue of running lead-free solder paste and leaded solder paste through reflow at the same time. The point with this would be to process all standard leaded components with Lead paste while also processi
Electronics Forum | Mon May 12 12:58:07 EDT 2014 | emeto
Hello all, I have a diode(gold plated)on some assemblies that gives me a a hard time. The paste is wetting too good and climbs the lead of the component and touches the body which is a defect. I just wonder what if there is a way to heat the board e
Electronics Forum | Mon May 12 15:13:29 EDT 2014 | emeto
Thank you guys. As we are speaking I keep examine the problem and here is what I got so far. 1. I measured the temperatures on my profile and the lead is hotter than the board. The lead goes 12 seconds earlier than the pad and is taking the solder.