Electronics Forum | Mon Jul 24 11:35:42 EDT 2006 | Jimk@ics-inc.org
We have experienced a problem with tin leaching or discoloration of lead terminals on random parts on solder side of a paste/paste operation. The profile has been used on previous production runs and there doesn't appear to be any heat damage to othe
Electronics Forum | Thu Feb 23 05:33:55 EST 2006 | teilo
Hi John We manufacture titanium component parts for wave solder machines inc retrofit kits for the conversion to lead free at a fraction of the manufacturers cost. For a quote email me at office@teiloengineering.com
Electronics Forum | Thu Jul 27 12:09:41 EDT 2000 | JohnW
Jason, where on the board is your connector?, front / back / middle? and where it on the PCB that you don't have issues with? Thief pad's are basically dummy pad's taht you have after the last set of pin's on the component are are used to draw the
Electronics Forum | Thu Jun 17 20:35:51 EDT 1999 | Earl Moon
| | | Does anyone know where I can find a list of things to do to when troubleshooting issues during the wave solder process? | | | | | | for example: | | | | | | Solder Bridge | | | 1.verify amount of flux been aplied. | | | 2.verify turbulance on
Electronics Forum | Mon Jun 21 14:55:27 EDT 1999 | JohnW
| | Does anyone know where I can find a list of things to do to when troubleshooting issues during the wave solder process? | | | | for example: | | | | Solder Bridge | | 1.verify amount of flux been aplied. | | 2.verify turbulance on your solder w
Electronics Forum | Thu Jun 17 15:18:54 EDT 1999 | Earl Moon
| Does anyone know where I can find a list of things to do to when troubleshooting issues during the wave solder process? | | for example: | | Solder Bridge | 1.verify amount of flux been aplied. | 2.verify turbulance on your solder wave. | 3.etc.
Electronics Forum | Thu Jun 17 19:52:57 EDT 1999 | Tony
| | Does anyone know where I can find a list of things to do to when troubleshooting issues during the wave solder process? | | | | for example: | | | | Solder Bridge | | 1.verify amount of flux been aplied. | | 2.verify turbulance on your solder w
Electronics Forum | Fri Sep 09 17:41:58 EDT 2005 | Wild Bill
Reflow and wave flow solders have to be changed more often because of contamination. Pb free PCB's don't solder as well so you will likely have to find a new process or supplier. The higher temperatures heat soak the components so they all need to be
Electronics Forum | Mon Jul 16 09:53:36 EDT 2007 | ed_faranda
Yes, you can use lead-free parts in a leaded process. And the other is true as well, no-lead free parts in a leaded process. BUT, you should not use leaded parts through a non-lead wave solder process and of course, your board will not be RoSH.
Electronics Forum | Mon Jul 16 10:17:22 EDT 2007 | realchunks
Yes you can use no-lead parts in a leaded process. Your solder joints will be weaker than they once were unless you change your solder paste. You can try to improve this by running a hotter reflow temp, but be careful since your flux was not design