Electronics Forum | Tue Sep 01 20:43:06 EDT 2009 | davef
Please explain "adhesion of soldering is not uniform at the tips (soldering ends)." For example: * Is the "tips (soldering ends)" the component leads? * What is the component? * What is the finish on the component? * What process is causing this issu
Electronics Forum | Thu May 24 01:46:45 EDT 2018 | wchen930
ME ! High quality , Fast lead time , Reasonable Cost it gotta be me www.lmpcb.com Free Quote gerber goes to wchen930@lmpcb.com
Electronics Forum | Thu Aug 31 09:07:38 EDT 2017 | hxamalia
Hello ALL Good day , it is Amalia from HX Circuit Technology Co.,Ltd in China, we are a prefessional PCB factory with many years. We are focusing on quick lead time for PCB with good service . please contact with me now ,thanks Email: amalia@hx-
Electronics Forum | Thu Jan 14 04:45:16 EST 2016 | saimen
Hi There , Glad to contact with you , Here is Saimen in Tianweisheng , wish we will have a good cooperation in the furture if we have the honor . Our company is one of the largest custom-made PCB manufacturer in China. We can OEM,ODM,EMS single side
Electronics Forum | Wed May 31 20:56:54 EDT 2017 | juliefarrell
Maxim, I would like to help you. My company ICAPE has 35 PCB manufacturing partners in China. We can beat any price hands down. Full service provider. I can deliver you great price, good quality as well as lead time. You can imagine with 35 partn
Electronics Forum | Mon Jan 30 05:58:39 EST 2017 | rob
Hi all, > > Am new to SMT here. > > I have a very > thin laminate substrate which around 120um > thickess. Being that thin, warpage is constantly > an issue for us. > > For the solder printing part, > we have a number of problems. > > Being s
Electronics Forum | Thu Oct 05 15:58:16 EDT 2006 | RusH
Mario, Thanks for your response. We are building a leaded assembly with hot air leveled Sn/Pb pads on the PCB. In one case the component is a 7.5X5.2X1.8 wire wound ferrite inductor with Au/Sn leads. The second component is an 0808 Tantalum cap,
Electronics Forum | Fri Sep 09 17:41:58 EDT 2005 | Wild Bill
Reflow and wave flow solders have to be changed more often because of contamination. Pb free PCB's don't solder as well so you will likely have to find a new process or supplier. The higher temperatures heat soak the components so they all need to be
Electronics Forum | Fri Jul 27 10:07:18 EDT 2007 | rgduval
Our preference has been ENIG. We find that we achieve higher quality (visually) soldering for through hole and surface mount parts, with less handling issues than when we use white-tin, or immersion tin. We are about to do a test on some boards tha
Electronics Forum | Sat Jul 26 11:17:31 EDT 2008 | manishc
i am facing problem of pcb track lifing at B.G.A. after reflow.we r using lead free paste and fr-4 grade pcb with peak temp.about 270 deg.
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830