Electronics Forum | Tue Aug 14 15:45:06 EDT 2001 | davef
BOARD BAKING SCHEDULE: Bake time depends on the board thickness and construction. For laminated FR4 PCB, we bake between 6 and 24 hours at 100�C. ROOT CAUSE OF THE PROBLEM: Heating moisture entrapped between the laminations of the board too quickl
Electronics Forum | Wed Dec 22 11:12:33 EST 2004 | Steve
Does anyone have an opinion about the pro's and con's of Getek vs Isola FR408 laminate? What laminate to most of you call out? Thanks in advance for your feedback. Steve
Electronics Forum | Thu Feb 15 22:55:45 EST 2007 | davef
Questions are: * Is the blistering in the solder mask or the laminate? * If the blistering is in the solder mask, what do the blisters look like [eg, size, quantity, distribution, etc]? * If the blistering is in the laminate, what do the blisters loo
Electronics Forum | Thu Oct 15 14:23:31 EDT 1998 | Earl Moon
| I have a problem with measling on our PCB's. We saw it on our FR4 PCB's at final assembly yesterday. Is this a defect from the board vendor or something we did in our assembly process when building the PCA's (thru hole). Could the wave solder ma
Electronics Forum | Wed Jan 11 12:37:06 EST 2006 | Amol Kane
Hi all, hope everyonein the forum id doing fine and working diligently toward RoHS capability. One of my customers have asked me (my company) to recommend a lead-free laminate. us being a CEM, have no idea of design variables (df, dk etc., (process v
Electronics Forum | Thu Jan 31 09:08:27 EST 2008 | glezfl36
Since the implementation of the ROHS process in our Company with the higher temp requirements, we had observed an increase in problems related to delamination in the PCB's. Actually we are using FR408 and Gracescore materials and are changing to a Ve
Electronics Forum | Mon Aug 08 22:51:39 EDT 2005 | plcc
Hi Davef, The whole laminate turns yellowish.
Electronics Forum | Thu May 09 17:21:39 EDT 2002 | davef
In describing a bare board, you need to talk about base, laminate, and conductive materials. Common laminate materials are: * Glass fabric * Cotton fabric * Paper Common NEMA grades of technical laminates are: * Glass Fabric Grades: G3, G7, G10,
Electronics Forum | Thu Aug 29 06:39:29 EDT 2013 | claudiagreene
Many China PCB factories don't have the lamination equipments. Usually,they will send pcbs inner layer finished to other big factory or the lamanation factory to complete this process.It seems it is not what you like. But it is common... Is it ok for
Electronics Forum | Mon Feb 05 17:18:53 EST 2001 | davef
Wha, Nellie!!! Delamination & Blistering IPC-A-600D Although it may occasionally occur because of a severe process breakdown, delamination and blistering occurs as a result of an inherent weakness of the material. Either condition represents a brea
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830
.gif)
winsouce.jpg)