Electronics Forum | Fri Jul 27 10:07:18 EDT 2007 | rgduval
Our preference has been ENIG. We find that we achieve higher quality (visually) soldering for through hole and surface mount parts, with less handling issues than when we use white-tin, or immersion tin. We are about to do a test on some boards tha
Electronics Forum | Thu Oct 05 15:58:16 EDT 2006 | RusH
Mario, Thanks for your response. We are building a leaded assembly with hot air leveled Sn/Pb pads on the PCB. In one case the component is a 7.5X5.2X1.8 wire wound ferrite inductor with Au/Sn leads. The second component is an 0808 Tantalum cap,
Electronics Forum | Wed Jan 07 14:33:00 EST 2015 | eezday
The assumption that a HASL Sn63 PCB can be soldered with SAC solder paste is likely a bad one. The board itself is likely FR4 which can be damaged by lead free temperatures. The HASL finish isn't an issue from the perspective of it's makeup and actu
Electronics Forum | Tue Jan 06 16:31:41 EST 2015 | jacklucas
In switching to lead free processing, we find ourselves having over 400 PCB part numbers with Sn63 HASL finish. And there is no hope of quickly purging inventory and getting our drawings changed to call out a lead free finish. I want to avoid having
Electronics Forum | Wed Jan 07 15:48:22 EST 2015 | jacklucas
We switched our PCB's to 170Tg over 10 years ago, so we're probably good to go on the temperature aspect. Thanks for the opinion on the added lead content.
Electronics Forum | Tue Apr 26 15:21:11 EDT 2005 | russ
Sounds to me like they are thinking since they have a gold board that it must be processed lead free. This kind of thing is happening all over since OEMs are starting to think about pb free and sending their purchasing and engineering to these semin
Electronics Forum | Fri Jan 04 15:42:03 EST 2002 | nwyatt
There are several implications: - some lead free alloys do not form an acceptable solder joint when used with lead contaning paste. (ie. Bismuth) - if you use both lead free and lead containing components, you will have different solder joint compos
Electronics Forum | Fri May 28 17:44:51 EDT 1999 | Glenn Robertson
| I discovered that we have some gold plated (30 mico in.) through hole connectors which were Paste In Hole soldered (60 sec at reflow) on a HASL PCB. Do we have an embrittlement reliability issue? The calculated volume % of gold in the joints is abo
Electronics Forum | Fri May 28 17:30:35 EDT 1999 | Dave Clements
I discovered that we have some gold plated (30 mico in.) through hole connectors which were Paste In Hole soldered (60 sec at reflow) on a HASL PCB. Do we have an embrittlement reliability issue? The calculated volume % of gold in the joints is about
Electronics Forum | Thu Aug 13 16:46:13 EDT 2009 | snsmt
Hello Everyone, I have noticed that everytime that we have ran a PCB with fine pitch components (or even 0603s), there are little white strands on the leads or on top of the components. It occurs on both lead and lead free solder. We usually soak
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830