Electronics Forum | Wed Apr 01 11:41:34 EDT 2020 | emeto
Very interesting.Safety datasheet suggest acid that might turn yellowish. I am interested is it cleaned easily with water?
Electronics Forum | Sun Jun 22 13:24:49 EDT 2014 | davef
I don't know. We never had craziness like this before lead-free. You should have the yellowish-metal analyzed to be sure. Guessing: You're seeing this color on the terminations of components, not on the bulk of the SnX solder connection. If that's
Electronics Forum | Sun Jan 25 17:40:16 EST 2009 | cuperpeter
Hello All, I have a problem with nonwetting Au finish after second cycle of reflow soldering doublesided boards. Solder nonwetted pcb pads (is wicked to component terminations) Either these pads or some of non component pads became discoloured from
Electronics Forum | Tue Feb 03 16:42:50 EST 2009 | cuperpeter
Hello All, > > I have a problem with nonwetting Au > finish after second cycle of reflow soldering > doublesided boards. Solder nonwetted pcb pads (is > wicked to component terminations) Either these > pads or some of non component pads became
Electronics Forum | Wed Feb 26 04:28:39 EST 2014 | chongns
Hi All member I have a problem on the stable down the color of the white solder mask PCB. first, i tough the color differences was cause by the solder mask ink, but after a close look, the color change are cause by the copper under the solder mask
Electronics Forum | Tue Oct 03 17:04:07 EDT 2006 | cuculi54986@yahoo.com
Glenn, What alloy are you using for Pb-free HASL? You say tin copper nickel, but is it SN100C? Against manufacturing engineering's recommendation, my company specified simply "Pb-free HASL" as the finish for our Pb-free PCBs. One of our suppliers