Re: Adhesive strength specs

Electronics Forum | Sun Jan 11 12:03:51 EST 1998 | Bob Willis

As a basic guide the minimum spec you should look for is 500g you should achieve a force on most chip parts of 800-1000g. Parts are lost on wave soldering due to no material, poor curing, poor surface adhesion and poor handling. Its not the wave sold

Conformal over No-Clean

Electronics Forum | Fri Apr 26 09:32:22 EDT 2002 | blnorman

We conformally coat over NC solder paste. No problems. We're using a platinum catalyzed addition cure silicone. The only concern with this conformal coating is cure inhibition. You must test the coating over the residues to be sure there is no in

Solder joint strength

Electronics Forum | Wed Mar 30 16:07:24 EST 2005 | Dreamsniper

If there's no shear strength standard for solder joint, how will I define my pad width and length then. I have a 8.5 mils width and my component lead width is 8.66 mils based on manufacturer's minimum width specification. How will I identify that it

Same pattern of capacitor crack

Electronics Forum | Thu Nov 13 11:45:04 EST 2008 | pbarton

We have seen a similar problem. Turned out to be mechanical stress on the component caused by the method of location and clamping at ICT. Where is the component located on the assembly? Poorly adjusted clamping pillars on clamshell fixtures can cause

BGA Voiding for RoHS

Electronics Forum | Fri Nov 13 06:56:37 EST 2009 | CL

Good Morning, The customer is looking for void free connections. They had never specified an acceptable percentage. We are reacting to the test yield. Our yield has averaged 50%. We do not test the product so we rely on feeback from the customer. Us

Solder Joint Strength Comparison

Electronics Forum | Tue Sep 04 10:48:49 EDT 2007 | lloyd

How do other people check their solder joint strength after a process change? For example, say you are getting wetting problems and you feel that a change to the reflow profile may help, or perhaps a slight change to the stencil aperture to reduce so

Voiding in LGA (LT) soldering

Electronics Forum | Wed Sep 01 05:09:27 EDT 2010 | grahamcooper22

Dear SMT Manufacturer, I am wondering if the device could have so much moisture in it and storing it in a dry cabinet isn't going to remove it all. As a final test to see if moisture in the device is causing the voids/solder balls then I'd bake it a

Voids with LGAs

Electronics Forum | Fri Jan 18 12:34:14 EST 2013 | duchoang

Yes, I have. think I have pretty good reflow profile. We use Lead-Free,No-Clean,SAC305 Solder Paste. The problem is at LGA design.The pad size is alot bigger than BGA. They are totally flat and do not have balls/spheres which melted and collapsed thr

Re: Immersion Gold

Electronics Forum | Thu Sep 30 12:02:20 EDT 1999 | Wolfgang Busko

| I am having problems processing immersion gold boards. The achieved solder joints appear acceptable a la IPC-A-610, but the resultant joint does not fully cover the land, i.e. you can still see an outline of gold pad. | What is the best way to achi

Re: Solder Joint Strength

Electronics Forum | Tue May 26 13:01:40 EDT 1998 | Earl Moon

| Regardless of what various inspection standards state, has anyone got any information on how the strength of a soldered joint changes with the amount of solder in contact with the legs. ie if there is 0.152um depth of contact how does the joint st


lga shear test searches for Companies, Equipment, Machines, Suppliers & Information

Baja Bid Auction JUL 9-10, 2024

High Precision Fluid Dispensers
One stop service for all SMT and PCB needs

High Throughput Reflow Oven
PCB Handling Machine with CE

Best Reflow Oven
Global manufacturing solutions provider

Training online, at your facility, or at one of our worldwide training centers"
PCB Handling with CE

World's Best Reflow Oven Customizable for Unique Applications
Fully Automatic BGA Rework Station

"回流焊炉"