Electronics Forum | Mon Nov 15 15:27:48 EST 2004 | davef
In creating your solder balls, consider printing or dispensing solder paste on the pads of the LGA and then reflowing the paste.
Electronics Forum | Tue Jul 02 02:50:55 EDT 2002 | ianchan
Hi mates, was going thru the IPC-A-610C Standards, and noted BGA voids stands somewhere between 10%-25% voids permissible in the solder "ball" bump, after reflow process. Was wondering, hypothetical case study, is there any specification for voids
Electronics Forum | Thu May 09 18:06:42 EDT 2002 | bcceng
janchan, don't know how many LGA's/LCC/BCC's you are placing but a short term solution that I can recommend is the application of solder bumps to the component and than place it after board has gone through reflow or even at the same time. Our compa
Electronics Forum | Sun Mar 26 19:02:05 EST 2006 | ms
Hi We are running automatic stencil printers, open squeegees, stainless stencil, stainless blades, print speed 25-30mm/sec. We have a frustrating consistency issue printing .37x.3mm apertures on a 45pin LGA (11 pads each side, 1 large ground in mid
Electronics Forum | Thu Aug 24 06:58:19 EDT 2006 | davef
Darby National published stencil recommendations for their LGA in the "SMT Assembly Recommendations" section of: http://www.national.com/an/AN/AN-1187.pdf Is it possible that Silicon Laboratories published a similar document for your Cygnal CP2101?
Electronics Forum | Wed May 08 23:18:58 EDT 2002 | ianchan
Hi mates, have this SMT production issue : A) We have a leadless-chip-carrier(LCC) IC package that is classified under the Land-Grid-Array(LGA) package family. B) The LCC is 4mm x 4mm, and has 28 tin plated pads located beneath the outside perimet
Electronics Forum | Sun Apr 11 11:39:52 EDT 2010 | manchella
When we have sent some of motherboards for reliability testing in a tird party laoratory. It is found that when Dye&Pry is done after 600 cycles of Thermal Cycling, in LGA socket only one of the corner solder joing had 100% type 3 crack. All other so
Electronics Forum | Thu Sep 02 07:50:27 EDT 2010 | sachu_70
Just to add to my comments,solder joint voids do occur in LGA. Voids in LGA can be larger due to geometry and greater ratio of flux to solder. IPC-A-610D specifies a greater than 25% voided area is a defect for BGA, however, it does not specify the d
Electronics Forum | Mon Aug 10 12:28:17 EDT 2009 | davef
We don't know dip about your Linear Tech LGA118, but we agree with published reports that say you should have between 4800 and 7000 thou^3 of paste on the pad for a LGA. These volumes were analyzed based on volumes found successful for CGA and then e
Electronics Forum | Thu Sep 02 06:22:34 EDT 2010 | sachu_70
Good. This is the right way to profile. Let me ask you, have you anytime soldered QFN componets on your boards? The concept of LGA soldering is similar to that used for a QFN package. QFN soldering also exhibits void formations, and is an inherent pr