Electronics Forum | Tue Oct 10 13:32:26 EDT 2006 | rsteele
Does anyone know of any tests or testing done on the peel strength of components to pads. I have alot of info on FAB level peel strength testing, but nothing on components themselves. Is there any process(es) to test and insure new pastes and reflo
Electronics Forum | Wed Oct 11 09:53:06 EDT 2006 | Rob
Yes, kind of - I had a look through my notes from a while back where we did a lot of work on bending strenght but the only original source I could find was reference to a paper drawn up in 1979 "Increase Terminal to Pad-Peel Strength with a Standard
Electronics Forum | Thu Mar 13 01:42:58 EDT 2008 | Sean
Thanks Real Chunks and Davef...Yours input is valuable to me. My inputs towards your question asked below: Questions are: * Why did you tell us the following? "This BGA is installed with heatsink (with hook at both side of the heat sink) manually b
Electronics Forum | Fri Nov 22 08:57:56 EST 2002 | davef
Q1: What do you mean by "if the board is manufactured properly"? A2: If the epoxy is noy cured prooperly, for instance, the copper will not be well attached to the glass. So, peel strength will be lower. Q2: I don't believe that the peel off/or lif
Electronics Forum | Wed Nov 20 21:04:15 EST 2002 | yngwie
Hi Dave, What do you mean by "if the board is manufactured properly". If the board is not manufactured properly, humidity will have an impact on the peel strength? Is that what you mean. How does the Humidity impacted the peel strength ? Thru' which
Electronics Forum | Wed Nov 20 16:53:18 EST 2002 | davef
Q1: How important is the bare PCB baking ? A1: Baking boards is a non-value added activity. Q2: What is the temperature for baking @ what RH ? A2: Search the fine SMTnet Arcives for bake recipes. Q3: What would be the impact for the ENTEK finishe
Electronics Forum | Mon Nov 15 21:35:50 EST 1999 | Dave F
Bob Bob: Fortunately, you found this before you built-up a lot of product. Some thoughs and other drivel: 1 Use IPC-TM-650, Method 2.4.8 for copper peel with a Instron machine. Typical pad peel strength requirement for FR-4, 2 oz. copper is: 6 l