Electronics Forum | Sat May 30 08:24:09 EDT 1998 | Dave F
| | | | We recently made the switch to no-clean and the wurface mount is turning out beautifully. However, the wave solder process continues to put up a fight; we are getting a white residue on the surface of the PCB. The residue is not locali
Electronics Forum | Sat May 30 12:51:29 EDT 1998 | Earl Moon
| | | | | We recently made the switch to no-clean and the wurface mount is turning out beautifully. However, the wave solder process continues to put up a fight; we are getting a white residue on the surface of the PCB. The residue is not loca
Electronics Forum | Mon Sep 17 17:09:32 EDT 2001 | jschake
Flux: No-clean pastes tend to have a wider print process window in terms of print speed and pressure. More importantly, no-clean pastes are more tolerant to changes in temperature and humidity. They also exhibit longer stencil life than water-solub
Electronics Forum | Sun Apr 14 00:04:50 EDT 2002 | lysik
Just to let all the folks no. If you register (and pay the fee) a machine with any (OEM) company in the USA You have the same rights as a new user. Companies like UIC, Gen Rad, Agilent, etc came up with these fees to discourage buying used equipment.
Electronics Forum | Fri Jun 14 14:25:05 EDT 2002 | davef
Good job clarifying things. So, your MELF are just rolling off the pads. So much for the rocket scientist that talked you into those �V� shaped apertures, eh? [Or taking it the other way: Wow, just think how bad it would be if they weren�t worki
Electronics Forum | Tue Aug 20 18:15:02 EDT 2002 | davef
Haaaaa!!!! Soldering to plastic!!!! An apt analogy!!! I like to compare it to soldering to dirt. Some thing. In fact, you are soldering on nickel, when soldering on many things. It�s just that the gold, er Pd, flash enables the wetting mechanism
Electronics Forum | Fri Oct 18 09:50:02 EDT 2002 | russ
Steve, I am not aware of any standards so to speak. But IPC 782 and 770 have some useful info regarding mounting and pad geometries for wave etc... Since I do not know what type of components you will be wave soldering I will just give you some
Electronics Forum | Fri Nov 22 10:38:30 EST 2002 | slthomas
The follwing is from the Technet archives, per IPC's Jack Crawford. I dug it up during some investigation of a supplier's issues with humidity in an Asian plant: There is support for this in IPD-HDBK-001 w/Amendment 1 Handbook and Guide to Suppleme
Electronics Forum | Thu Dec 26 16:51:47 EST 2002 | davef
First, an earlier poster suggested using DI water. We are NOT excited about DI water with a NC fluxer, unless DI water is the proper flux thinner. Second, as you inplied, the maintenance steps you take should vary according to the amount of time th
Electronics Forum | Thu Mar 06 01:32:10 EST 2003 | kenBliss
gregp Your question started out asking about the advantages of bulk feeding. Based on the discussion it all comes down to costs. I offer another perspective that I believe is extremely relevant. Any advantage in manufacturing has to come down to