Electronics Forum | Mon Oct 29 12:44:33 EDT 2018 | robl
Hi Reckless, If it's a Standard Phillips Sapphire then no, they are not a beginner machine. The feeders have to be spot on and the machine requires a much longer service as they have 2 sets of 12 heads. Spares will start becoming harder to get soon
Electronics Forum | Tue Jul 03 10:20:15 EDT 2018 | yannis
Our firm is SMT factory exclude design, components are selected by customers. We are going on a project by studying the solderability life of warranty at least 3 year for customers requirement. The theory is if the workmanship is good enough, then th
Electronics Forum | Sun Feb 24 11:16:12 EST 2019 | proy
Guys, I have been down this road also spent a lot of time working on this. Electrolytics often are difficult to solder like this. For the sake of testing, try a water soluble more active flux as an initial test. IF you compare hand solder wetting the
Electronics Forum | Thu Jun 27 08:47:21 EDT 2019 | SMTA-John
Having success with Circuit Boards #432 Solvent Resistant Ink - Designed specifically for circuit boards. This medium dry ink is highly resistant to solvents .... It is also non-conducting. Note: this ink contains an aggressive solvent so should not
Electronics Forum | Wed May 15 09:33:16 EDT 2019 | kahrpr
All manufactures ratings on machines are way over blown. I am not shilling for Hanwha we have there equipment it runs good our SM471 averages 36k to 42k. there is so much that goes into how fast a machine runs such as board design type of parts, pane
Electronics Forum | Wed May 08 18:04:02 EDT 2019 | slthomas
You would have to do some extensive testing to really now for sure how much better coated blades perform than OEM blades. Deciding whether or not they last longer is just a function of regular inspections under a scope and accounting for the number
Electronics Forum | Mon Dec 30 12:55:37 EST 2019 | emeto
We saw your profile, which in my opinion looks alright based on the guideline from the vendor. Can you tell us more about the joints that you cleaned? Are they showing nice wetting and nice and shiny finish? How about your stencil thickness? From my
Electronics Forum | Thu Jan 09 13:18:15 EST 2020 | charliedci
We have been experiencing an issue with solder balls coming out of wave, both RoHS and 63/37, no clean process. It has been determined that a reduction in flux has all but eliminated the solder balls except for where we need to use board stiffeners a
Electronics Forum | Tue Feb 04 10:25:48 EST 2020 | rgduval
You'll probably need Mycronic/Aegis input on your issues with the software. When I was doing it a few years ago, the software interface was a lite version of CircuitCam, but, I was under the impression that Mycronic was going to deprecate that softw
Electronics Forum | Mon Feb 03 16:26:30 EST 2020 | stephendo
A few lifetimes ago I went to a seminar on reflow profiles. The speaker emphasized more than once that the cool down rate is important. Someone asked him about controlling the cool down rate and he acknowledged that you can't. And IIRC it was an ove