Electronics Forum | Mon Oct 18 22:15:11 EDT 2004 | KEN
I have two industry leading customers that have specific requirements for components to survive 30 seconds above 230C. In one case I have a custom ASIC that is heat sinked on the die (to the PCB). The sink pulls heat out of the lead frame very effi
Electronics Forum | Mon Oct 18 12:02:06 EDT 2004 | Rob
Hi Guy's, Sorry about this, but yes it's another lead free related question. We are looking at using a Chinese SMD DC-DC Converter in a new design, whilst keeping one eye on the approaching Lead-free issue. The manufacturer claims that these are O
Electronics Forum | Sat Jan 15 10:45:04 EST 2005 | Brad
HI, I actually have ask the same question a while back. Yes, using lead free component in a leaded process should be no problem at all. May required just a little hotter peak temp. during reflow, to achive optimal solderability.
Electronics Forum | Mon Jan 17 11:23:49 EST 2005 | Brad
Ya Russ is right for Ti Parts they tend to use more pelladium, which requires a bit more heat average temp increase is about 10 degrees C. from 225-235. As far as optimum solder joint I look for fillets on all sides of leads. The back of the lead is
Electronics Forum | Sun Feb 05 08:41:15 EST 2006 | Cmiller
Are you refering to reflow soldering or wave soldering? Brian, do you have any data to support that SAC305 is more reliable than Tin-Copper-Nickel? NEMI reccomended SAC type alloys for reflow and Tin-Copper for wave. See: http://circuitsassembly.
Electronics Forum | Fri Aug 31 13:51:33 EDT 2012 | joeherz
First off - There should be no issue with washing your OA/water soluble boards with the other customer's no clean units provided that the recipe being used has been validated to effectively clean each product. If your supplier is using a batch syste
Electronics Forum | Thu Dec 06 23:34:25 EST 2001 | Beny
Pls. help. I�ve problem with non-wetting defect at capacitor termination. I have faced this problem at the 2 kinds of termination. One is chip capacitor 0603 that its outer termination surface composed with 100 Sn (Lead free) and another one is Sta
Electronics Forum | Tue Feb 06 21:43:11 EST 2007 | Wayne
If it is instructed to ship lead free product to customer, then low temp lead free solder paste can be considered. For example, Viromet solder paste from Singapore Asahi (peak temp is between 220 to 225 degree C).
Electronics Forum | Mon Jan 29 10:11:12 EST 2007 | muse95
What does your customer want you to do? I would not want a CM soldering one of my boards with leadfree paste if I didn't ask him to. Whatever you do, get approval first. Two things to consider: If the other components are not rated for leadfree tem
Electronics Forum | Fri Feb 23 09:55:02 EST 2024 | carl_p
Got you. 225C for peak does seem low to me. Henkle is the main one i've used with a peak of 245c & Alpha around the same although I try to keep that at no higher than 235C as we use it for LED arrays. If the peak is that low, is the liquidus te
COT specializes in high quality SMT nozzles and consumables for pick and place machines. We provide special engineering design service of custom nozzles for those unique and odd components.
2481 Hilton Drive
Gainesville, GA USA
Phone: (770) 538-0411