Electronics Forum | Fri Oct 19 10:49:48 EDT 2007 | brulal1
Hi I will like to know what do you think about cleaning hand solder, my employee spend about 25% of they time to brush they hand solder with teddy pen cleaner, we used no clean solder wire. It�s not been the first time that I try to eliminate those c
Electronics Forum | Mon Oct 22 15:41:39 EDT 2007 | davef
Bruno The real question about your troop using Kester 951 wave solder flux on boards is: how is the flux applied and controlled. See, when you apply this flux with your wave solder fluxer, it is ideally applied in a metered fashion with your fluxer
Electronics Forum | Tue Aug 10 03:13:30 EDT 1999 | Dreamsniper
| hello to everybody, | we have a really satisfactory no clean process, both smt/reflow and wave soldering, but we get troubles with defects rework; | does anybody know how to eliminate flux residues or how not to produce them during rework operatio
Electronics Forum | Fri Oct 19 11:51:25 EDT 2007 | rgduval
By definition, no clean solder can be not-cleaned. The solder/flux are formulated to result in low ionic-contamination, hence, no cleaning. I have, however, always had at least one customer that requests their no-clean solder get cleaned. No-clean
Electronics Forum | Fri Oct 26 07:41:26 EDT 2007 | bbl
We recently changed to an Amtech no clean paste and flux that is washable. So far excellent results. Far superior to the water soluable paste we were using. Fewer solder balls, longer life in printer, boards can be left up to 5 days and still come
Electronics Forum | Tue Aug 10 05:51:03 EDT 1999 | Gian.D
| | hello to everybody, | | we have a really satisfactory no clean process, both smt/reflow and wave soldering, but we get troubles with defects rework; | | does anybody know how to eliminate flux residues or how not to produce them during rework op
Electronics Forum | Mon Aug 09 10:10:29 EDT 1999 | Gian.D
hello to everybody, we have a really satisfactory no clean process, both smt/reflow and wave soldering, but we get troubles with defects rework; does anybody know how to eliminate flux residues or how not to produce them during rework operations? Th
Electronics Forum | Tue Aug 10 07:47:12 EDT 1999 | Brian
| | | hello to everybody, | | | we have a really satisfactory no clean process, both smt/reflow and wave soldering, but we get troubles with defects rework; | | | does anybody know how to eliminate flux residues or how not to produce them during rew
Electronics Forum | Tue Aug 10 20:22:15 EDT 1999 | Wayne Sanita
Hello, Could be that touchup operators are using too much flux. What are you dispensing flux with. Disposable or refillable flux pens are good to have around. | | | | hello to everybody, | | | | we have a really satisfactory no clean proc
Electronics Forum | Thu Aug 12 09:02:08 EDT 1999 | Gian.D
| Hello, | | Could be that touchup operators are using too much flux. What are you dispensing flux with. Disposable or refillable flux pens are good to have around. | |Good! could you suggest some suppliers name or address or web site or e.mail...