Electronics Forum | Mon Jan 29 12:42:24 EST 2001 | davef
Several points about your query are: * TI�s solderability protection specification is a minimum of 3 u" of palladium over 40-60 u" of nickel plate over a http://www.ti.com/sc/docs/products/logic/package/palladm/index.htm
Electronics Forum | Mon Jan 29 06:44:59 EST 2001 | Scott B
I have recently come across a device which has a palladium over nickel finish which when soldered shows evidence of poor wetting to the lead ( i.e. a wetting angle greater than 90�) about three quarters of the way up the side of lead. This is only vi
Electronics Forum | Thu Jul 15 06:27:50 EDT 2010 | xps
Hi after an enviromental test 85C/85RH, for 3 months (powered), of an electronic assembly with edge finger tabs ENIG finished (nickel 5micron, gold 0.02micron), the nickel disappears completely under the gold (due to corrosion, I think). Does anyone
Electronics Forum | Thu Mar 31 17:27:36 EST 2005 | russ
Are we possibly talking palladium instead of platinum? I haven't yet heard of platinum terminations (seems expensive) If it is palladium over nickel, I can tell you that you need to reach 225-230 Deg. C in reflow and the TAL should be about 90 sec.
Electronics Forum | Thu Mar 31 19:52:50 EST 2005 | davef
We agree with Russ that you're talking palladium instead of platinum. Your wetting problem likely is not the Pd-Ag surface layers, but the underlying metal or nickel to which you need to wet. Either a base metal is: * Contaminated and poorly wettabl
Electronics Forum | Mon Mar 30 08:11:22 EST 1998 | Derek Drabenstadt
Does anyone have any experience with fired-silver/platinum/palladium lead terminations soldering. I have had issues on nickel over gold plated boards but not with HASL'd boards with tin/lead pads. Is this the norm?
Electronics Forum | Tue May 14 22:09:04 EDT 2013 | ultimatejoker
Hi, what is significant different between PdNi and PdCo Plating? I found in some papers indicate that the deposit characteristics for both plating is totally the same.
Electronics Forum | Mon Jan 25 13:39:51 EST 2021 | grahamcooper22
Thanks for your reply. According to the manufacturer there isn't any palladium under the solderable coating on the chips...just nickel....i guess maybe the nickel is heavily oxidised. I have experienced the poor solubility (zero solubility at 210 deg
Electronics Forum | Wed Feb 25 17:02:05 EST 1998 | Doug Romm
Just a comment to clarify this discussion. Typically chip caps and other passive components that use palladium plated to the end of the component are very different from the TI nickel/palladium plated IC components (leaded devices). The main di
Electronics Forum | Mon Aug 27 08:03:32 EDT 2007 | davef
Actually, you will be soldering and wire bonding to the palladium layer, so we should have asked if you checked that layer, rather than the nickel. We not sure of the source of the copper that your see on EDX. It's possible copper from the pad migra