Electronics Forum | Fri Apr 01 10:35:09 EST 2005 | shannond
Definitely platinum http://www.omega.com/Temperature/pdf/1PT100FR_RTD_ELEMENTS.pdf
Electronics Forum | Thu Mar 31 19:52:50 EST 2005 | davef
We agree with Russ that you're talking palladium instead of platinum. Your wetting problem likely is not the Pd-Ag surface layers, but the underlying metal or nickel to which you need to wet. Either a base metal is: * Contaminated and poorly wettabl
Electronics Forum | Thu Aug 29 20:02:58 EDT 2002 | davef
Often assemblers leave areas unsoldered for future component additions, modifications, and test points. On imm silver boards, these unsoldered areas become a real bear to solder/test later in life. One way to avoid that problem is deposit some solder
Electronics Forum | Fri Aug 30 04:44:31 EDT 2002 | jason
Hi Dave, Why does it become " a bear" if u leave it unsoldered ?? Does it oxidise or something ?? Question (1): Does Ag imm. PCB need to use Solder paste with AG ?? If yes, why. Question (2): Does Ag imm pcb have poorer surface finishes than HAS
Electronics Forum | Wed May 11 13:27:30 EDT 2005 | Sam Ho
i want to know which type of solder paste and reflow profile can support the solder pad with nickel but not covered gold on the pcb.
Electronics Forum | Wed May 11 13:50:30 EDT 2005 | russ
I would contact your paste supplier, bare nickel can be impossible to wet to. How oxidized is it?
Electronics Forum | Thu May 12 07:54:37 EDT 2005 | Rob
We talked about something similar here: http://www.smtnet.com//forums/index.cfm?fuseaction=view_thread&CFApp=1&Thread_ID=8051&#Message31805
Electronics Forum | Tue Aug 10 09:26:49 EDT 2004 | davef
You should be able to solder to brass - check with you flux supplier to get their recommendations. The flux you are using may not have enough activation to breakdown the oxides on the brass surface. A word of caution - brass (copper and zinc alloy)
Electronics Forum | Thu Jun 08 07:56:34 EDT 2017 | jkitt84
In an excellent previous thread davef mentions brass should be plated prior to soldering to prevent zinc leaching from the brass. It is reported once the zinc leaches, the joint is weak. He recommends copper or nickel plating. Would silver plating w
Electronics Forum | Sun Mar 31 10:03:25 EST 2002 | Bob
Cheers Dave, to answer some of your questions. � The component lead is copper with a tin / lead coating. The pads are standard Copper / Nickel / Gold. � The solder is standard Tin / Lead / Silver (2%) We have a lab that can determine the composition