Electronics Forum | Thu Oct 30 21:55:13 EDT 2014 | davef
Why soldering issues? I'd guess the nickel is corroded. It is very difficult to solder to oxidized nickel. Your SAC305 would get kicked all the way down the conveyor by nickel oxide. A lack of Ni-Sn-IMC formation will confirm this dewetting . What's
Electronics Forum | Mon Oct 27 20:01:00 EDT 2014 | rangarajd
Hello, We are facing solderability issues on a particular lot of board. THe Nickel thickness measured with an XRF is around 400 U inches. Spec calls out for 130 u inches Nickel and 3 - 5 U inches gold over it. Assuming there is no porosity on the g
Electronics Forum | Tue Apr 22 12:33:35 EDT 2014 | barryg
No we have a battery spring that is soldered directly to a PCB (standard tin plated copper PCB). The Battery spring supplier (and I have no confirmation he makes them or buys them) claims they are tin plated. When trying to solder to them it is very
Electronics Forum | Fri Apr 25 14:49:34 EDT 2014 | isd_jwendell
If the tab is Sn plated, you can solder to it as long as your iron has enough power (watts). If you continue to have trouble then it probably isn't Sn plated.
Electronics Forum | Mon Apr 21 16:38:45 EDT 2014 | barryg
Hello all. We have been having some problems soldering to what we believe is a nickel plated spring steel battery terminal to a PCB. We have tried scrapping , then tinning, dipping and still have problems. Are there any special fluxes or pre-treats t
Electronics Forum | Tue Apr 22 08:55:54 EDT 2014 | davef
I assume that you're talking about wanting to solder to metal tabs that are spot welded to the battery terminal. These tabs are not meant to be soldered. The metal was special selected for welding. In the old days, you could buy plumbing flux at th
Electronics Forum | Thu Oct 30 18:10:19 EDT 2014 | hegemon
Rather than asking why, maybe the better response is to reject the PWBs and have them re-fabricated correctly? Of course circular reasoning tells me that the reason for your issues is that you have 3x the amount of nickel beneath the gold. I wish I
Electronics Forum | Thu Oct 18 11:20:52 EDT 2001 | furrer
1. Does anyone has seen results for the reliability of Solder Paste containing less than 1% Silver. (It is in use for soldering 0402 components because of Tombstones. 2. Is it common to use eutectic Solder Paste SnPb, without any silver, for regular
Electronics Forum | Thu Jan 16 17:54:12 EST 2003 | Ren�
Hi burb , reflow temps are same than other profiles just follow your solder paste recomendations , Will help you a lot a solder paste with Silver , or if you want to eliminate completely the granular looking , use nitrogen with your oven ( You will s
Electronics Forum | Sun Jul 04 19:49:05 EDT 2004 | indy
Hello Everyone, We are having some problem with Palladium-Silver surface finish. We have ceramic components with the above surface finish. When we try to assemble these on Sn/Pb solder, we are observing open joints. If we reflow the compt for more t