Electronics Forum | Thu Aug 12 18:06:09 EDT 2004 | SR
May I ask what component types you are using and who the suppliers are? FYI - If the components have exceeded their shelf life, they may have oxidized too much for soldering using low activity fluxes. Thanks and best regards, SR
Electronics Forum | Fri Aug 13 16:54:20 EDT 2004 | davef
If the terminations on your components are not barrier plated, you must be very careful about the amount of time you stay above liquidous. As you'd expect, longer is not better. The longer you stay at liquidous, the more of the component terminatio
Electronics Forum | Mon Sep 22 15:32:20 EDT 2008 | davef
We see this fairly often. It doesn't affect solderability. Our analysis makes us think this coloration is copper. The reason copper appears on the surface may be that heat cycles increase the thinness and porosity of the immersion silver [IAg] coatin
Electronics Forum | Fri Jan 24 11:05:38 EST 2003 | johnw
I fyour just using Sn/Pb in your paste even using nitrogen will lave you with slightly grainy joints. The silver from your PCB will disolve into the Sn/Pb at 'uncontrolled' rate what I mean is depending on the temperature and time above liquidous the
Electronics Forum | Wed Apr 07 09:23:20 EDT 2004 | davef
In addition to your concerns about leaching, why aren't you concerned about: * Tin whiskers * Total absence of in use reliability information about no-lead, especially given that creep is significantly different between SnPb and no-leads. While they
Electronics Forum | Thu Apr 14 06:00:01 EDT 2005 | bryan
The shelf life of immersion silver is 6 to 12 months in good storage conditions. The finish is usually coated with a protective layer that inhibits oxidation (like with copper OSP). Care must be taken when handling the boards as the protective la
Electronics Forum | Fri Jan 24 19:19:11 EST 2003 | MA/NY DDave
Hi Don't really know what "your grainy" means. It could be good, marginal, or bad. You need to get some photos or micrographs of what is normal and off-normal. Compared to Sn/Pb 63/37 on mostly Sn it should look visually different. Every time you c
Electronics Forum | Fri Aug 11 22:14:59 EDT 2017 | dawson
Hi Adonys, What's ICP 1-3? Do you mean IPC? 1. Excess Plating- no excess, but filled with something which generated in the process of copper plating. 2. Dark Vias - it's oxidized. and the solder mask printing is not aligned. The board is failed. M
Electronics Forum | Tue Jul 13 16:35:25 EDT 2004 | Richard
Sounds like your Si plalladium finish has oxide on it from the firing or sitting around too long. I used to assemble LTCC and have had plenty of dealings with this matter. The best and easiest is to get an active type flux and solder paste. AIM makes
Electronics Forum | Thu Apr 22 17:19:57 EDT 1999 | JohnW
| | We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have t