Electronics Forum | Tue Nov 29 22:32:51 EST 2005 | davef
The dissolution rate of nickel into tin is a lot slower than that of copper [into tin]. This results in a nickel-tin (Ni3Sn4) intermetallic that is only 0.25-0.75�m thin after a normal soldering process. The Ni-Sn intermetallic compound tends to be m
Electronics Forum | Thu Mar 31 17:27:36 EST 2005 | russ
Are we possibly talking palladium instead of platinum? I haven't yet heard of platinum terminations (seems expensive) If it is palladium over nickel, I can tell you that you need to reach 225-230 Deg. C in reflow and the TAL should be about 90 sec.
Electronics Forum | Tue Apr 22 12:33:35 EDT 2014 | barryg
No we have a battery spring that is soldered directly to a PCB (standard tin plated copper PCB). The Battery spring supplier (and I have no confirmation he makes them or buys them) claims they are tin plated. When trying to solder to them it is very
Electronics Forum | Mon Apr 21 16:38:45 EDT 2014 | barryg
Hello all. We have been having some problems soldering to what we believe is a nickel plated spring steel battery terminal to a PCB. We have tried scrapping , then tinning, dipping and still have problems. Are there any special fluxes or pre-treats t
Electronics Forum | Fri Feb 03 17:47:06 EST 2006 | Brian Smith
Kester offers Tin-Copper AND Tin-Copper-Nickel. The Kester K100 alloy is a Tin-Copper-Nickel material that is very similar to SN100C. Straight Tin-Copper isn't tremendously popular but can be used in low-cost, consumer-electronics applications wher
Electronics Forum | Fri Jan 27 11:30:47 EST 2006 | solderiron
Kester is offering a tin/copper alloy for lead free. Any comments regarding using just tin/copper as opposed to tin/silver/copper or tin/nickel/copper? the price is low but why wouldn't everyone else offer just this alloy as opposed to the standard S
Electronics Forum | Sun Feb 05 08:41:15 EST 2006 | Cmiller
Are you refering to reflow soldering or wave soldering? Brian, do you have any data to support that SAC305 is more reliable than Tin-Copper-Nickel? NEMI reccomended SAC type alloys for reflow and Tin-Copper for wave. See: http://circuitsassembly.
Electronics Forum | Wed Aug 05 07:46:46 EDT 1998 | Earl Moon
| We have mixed to negative feelings about Omikron, but I beileve it is due to problems with the board fabricator rather than the process itself. When done properly, our Omikron boards have had very good solderability. However, we have had several
Electronics Forum | Thu Nov 13 20:48:04 EST 2003 | davef
There a number of studies like this published by component fabricators. Many can be found on the net. For instance: http://www.amd.com/us-en/assets/content_type/DownloadableAssets/Pb-free_Board-level_reliability_study.pdf
Electronics Forum | Tue Nov 11 12:49:13 EST 2003 | Carol
Could you direct me to a Standard or Study that has used this termination with 67/37 tin/lead solder please? I am looking for the recommended reflow temperature requirements and reliability issues for the completed product. We are receiving this type
.gif)