Electronics Forum | Fri May 21 20:38:40 EDT 2004 | Grant Petty
Hi, This would be a very exciting idea. Nitrogen is an inert gas, so this is why it's used, however Hydrogen mixed with oxygen in normal air is highly explosive, so it would be one of the worst gasses to use in a reflow oven I would think. Remember
Electronics Forum | Thu Mar 17 11:15:26 EDT 2011 | circleprime
I did some investigating and it seemed that getting a reflow oven with an inert atmosphere could be the answer to the inconsistant wetting issues that we are having with a leadfree DFN-10 on one of our products. Here's my question(s). It seems that
Electronics Forum | Tue Mar 09 07:06:42 EST 1999 | Charles Stringer
| | | | I need to setup an oven to run with a nitrogen atmosphere for | | boards with BGA's, but our ovens do not have the optional atmosphere monitor and controller. Is there a good way to sample and control the atmosphere without the optional bui
Electronics Forum | Wed Aug 04 18:57:26 EDT 1999 | Dreamsniper
| What oven temperature should be used to reflow solder (Sn63Pb37) on a PC board (0.075" to 0.100" thickness) in 5 to 10 minutes? | Hi Judy, In profiling you need an understanding of the reflow specs from the solder paste manufacturer then you nee
Electronics Forum | Tue Nov 01 15:26:43 EST 2005 | GS
Is it this your first experience of C-CGA RWK ? In order to approach a RWK of this kind of pakage it requires a capable process and clear operating procedure. In the past, the company who I use to work for, we rwkd plenty of this kind of CCGA. Earl
Electronics Forum | Mon Jan 04 18:56:25 EST 1999 | Marc P.
| We have a Vitronics SMR400N oven and many times need to use N2 inerting. My problem is that it takes close to an hour of operation to purge the system to achieve the desired O2 levels (~40PPM). This is not only time consuming but results in an inor