Electronics Forum | Wed Aug 27 15:49:43 EDT 2008 | grics
I think WML ought to have some photos on how to do this...
Electronics Forum | Wed Aug 27 22:54:44 EDT 2008 | omid_juve
what is WML ? can you please explain more
Electronics Forum | Thu Aug 28 16:21:23 EDT 2008 | realchunks
Larry, I'm seeing a pattern here of you and fire!?!?! What gives?
Electronics Forum | Mon Jul 08 03:09:12 EDT 2002 | Benny
Hi all How can I find the technical paper or source of information about using No-clean flux with high frequency apllication. High frequency mean more than 2 GHz - 5 GHz. I heard from my colleague that No-clean flux residue on board effect to high
Electronics Forum | Thu Aug 28 09:30:20 EDT 2008 | patrickbruneel
Omid, No-clean fluxes need to be used right out of the can without thinning. In the past with RA and RMA fluxes you could adjust or thin them to your desired density because they had plenty of solids up to 30%. No-Clean fluxes have a lot lower solid
Electronics Forum | Thu Aug 28 16:03:08 EDT 2008 | wavemasterlarry
I guess you're adding the gas to keep the fingers clean - sounds likeyou got your threads mixed up on the Forum. Any way I would suggest not doing this. Gas is pretty flammable. I have pix of one our Hollis cleaning machines going up in flames cau
Electronics Forum | Wed Aug 27 14:58:21 EDT 2008 | omid_juve
we have problem in setting the density of a no clean flux for using before wave soldering . first we dilute the flux but we have many short circuit problem between the pads of edge connector,then we densify the flux all the short circuit is removed b
Electronics Forum | Mon Jul 08 08:03:30 EDT 2002 | davef
http://www.goapex.org/html/S32-1_Csonka-Peeren.pdf
Electronics Forum | Fri Sep 05 13:49:04 EDT 2008 | gregoryyork
Tell the board shop to increase the cure temp of the resist as it is undecured especially if you have waxy/greasy resiues on the board and a brown tar like substence in the solder wave itself. If undercured then solder will not flow off the resist pr
Electronics Forum | Wed Feb 26 23:59:48 EST 2003 | Mike Konrad
Grant, No-Clean paste + IPA = White Residue! #1: Stop using IPA #2: Switch to either a solvent-based de-fluxing chemical or an aqueous-based de-fluxing chemical. If you are using an ultrasonic cleaner for your boards as stated, do not use sapon