Electronics Forum | Wed Aug 10 07:55:21 EDT 2005 | ajaydoshi
we are using heareous F381, F352 no clean solder paste. specially in qfp for high frequency board we observe that cleaing / removing of ' no clean flux 'is require. if we do not clean same most of time after all test & envioumental test it shows pin
Electronics Forum | Wed Aug 10 08:10:39 EDT 2005 | davef
Comments are: * Sounds like it's necessary to clean "heareous F381, F352 no clean solder paste" in your application. Consider a paste that may be better suited to your application. * If you're cleaning "low residue flux", consider using an organic ac
Electronics Forum | Thu Aug 28 09:30:20 EDT 2008 | patrickbruneel
Omid, No-clean fluxes need to be used right out of the can without thinning. In the past with RA and RMA fluxes you could adjust or thin them to your desired density because they had plenty of solids up to 30%. No-Clean fluxes have a lot lower solid
Electronics Forum | Mon Jul 08 03:09:12 EDT 2002 | Benny
Hi all How can I find the technical paper or source of information about using No-clean flux with high frequency apllication. High frequency mean more than 2 GHz - 5 GHz. I heard from my colleague that No-clean flux residue on board effect to high
Electronics Forum | Fri Oct 26 07:41:26 EDT 2007 | bbl
We recently changed to an Amtech no clean paste and flux that is washable. So far excellent results. Far superior to the water soluable paste we were using. Fewer solder balls, longer life in printer, boards can be left up to 5 days and still come
Electronics Forum | Tue Aug 10 20:22:15 EDT 1999 | Wayne Sanita
Hello, Could be that touchup operators are using too much flux. What are you dispensing flux with. Disposable or refillable flux pens are good to have around. | | | | hello to everybody, | | | | we have a really satisfactory no clean proc
Electronics Forum | Tue Aug 10 03:13:30 EDT 1999 | Dreamsniper
| hello to everybody, | we have a really satisfactory no clean process, both smt/reflow and wave soldering, but we get troubles with defects rework; | does anybody know how to eliminate flux residues or how not to produce them during rework operatio
Electronics Forum | Tue Aug 10 05:51:03 EDT 1999 | Gian.D
| | hello to everybody, | | we have a really satisfactory no clean process, both smt/reflow and wave soldering, but we get troubles with defects rework; | | does anybody know how to eliminate flux residues or how not to produce them during rework op
Electronics Forum | Thu Aug 12 09:02:08 EDT 1999 | Gian.D
| Hello, | | Could be that touchup operators are using too much flux. What are you dispensing flux with. Disposable or refillable flux pens are good to have around. | |Good! could you suggest some suppliers name or address or web site or e.mail...
Electronics Forum | Tue Aug 10 07:47:12 EDT 1999 | Brian
| | | hello to everybody, | | | we have a really satisfactory no clean process, both smt/reflow and wave soldering, but we get troubles with defects rework; | | | does anybody know how to eliminate flux residues or how not to produce them during rew