Electronics Forum | Tue Apr 06 09:50:58 EDT 1999 | Justin Medernach
| Does anybody put QFP's on the backsides of boards? Can they be reflowed without falling off? Do you use adhesive? | I use a double sided reflow process all day, everyday. I've hung QFP240s with embedded heat sinks and they don't fall off. Yei
Electronics Forum | Sat Aug 26 12:26:57 EDT 2000 | Ramon I Garcia C
Hi friends: I have a problem in the process of one PCB, I have a lot of insuficients of solder in top of the board, this pcb already was working good, but sudenly began there isn't flow thru hole, I ran the profile and it was ok, if I inmerse i
Electronics Forum | Fri Sep 05 13:49:04 EDT 2008 | gregoryyork
Tell the board shop to increase the cure temp of the resist as it is undecured especially if you have waxy/greasy resiues on the board and a brown tar like substence in the solder wave itself. If undercured then solder will not flow off the resist pr
Electronics Forum | Tue Jun 10 01:09:37 EDT 2003 | iman
Hi! Thanks to you as the first replier! I do admit it "narrows" the information channels feedback flow by keeping this thread reply limited to "non-commercial" engineering folks, but I already have lotsa war stories from the salesmen around this reg
Electronics Forum | Thu Sep 26 20:43:51 EDT 2002 | davef
"OK. If the connection doesn't look like I expect it to look, how do I know that the metallurgy is correct?" Comments are: * There are no pictures that will get you though this. * You should expect that gold that is dissolved in Pb/Sn solder to make