Electronics Forum | Tue Apr 06 09:50:58 EDT 1999 | Justin Medernach
| Does anybody put QFP's on the backsides of boards? Can they be reflowed without falling off? Do you use adhesive? | I use a double sided reflow process all day, everyday. I've hung QFP240s with embedded heat sinks and they don't fall off. Yei
Electronics Forum | Sat Aug 26 12:26:57 EDT 2000 | Ramon I Garcia C
Hi friends: I have a problem in the process of one PCB, I have a lot of insuficients of solder in top of the board, this pcb already was working good, but sudenly began there isn't flow thru hole, I ran the profile and it was ok, if I inmerse i
Electronics Forum | Mon Jun 25 01:57:07 EDT 2001 | nifhail
We experienced a random no contact at ATE on our board. The board I'm building consist of 9 BGAs, all of them are OK except for one, intermittently the tester will prompt no-contact message. It's happened on a diff. I/O, but only happened on that pa
Electronics Forum | Fri Oct 19 10:49:48 EDT 2007 | brulal1
Hi I will like to know what do you think about cleaning hand solder, my employee spend about 25% of they time to brush they hand solder with teddy pen cleaner, we used no clean solder wire. It�s not been the first time that I try to eliminate those c
Electronics Forum | Fri Jun 29 23:10:02 EDT 2001 | Danial
Thanx for the reply guys!! The problem happened on only one PBGA, the balls are eutectic and the paste volume height is at 5.96 mil min. The stencil opening has been increased to 30 mil which initially was 20 mil. You guys are right!! One probable
Electronics Forum | Wed Jun 28 00:37:05 EDT 2006 | YQ Deng
Dear Davef, Please told me your Email address, then I send the photos to you. Thanks!
Electronics Forum | Fri Feb 11 01:36:22 EST 2005 | brown
OK I am counting someone knowing this. True or False, if my touch-up operators touch-up the smt solder joints too many times will this make the joint weaker? if yes why? and what happens to my intermetalic layer? I have insisted if it looks good don
Electronics Forum | Tue Jun 26 20:40:36 EDT 2001 | davef
Your profile seems reasonable, as you say. As CPI says: Sure it could be planiarity issues with the balls, but that is not something that makes me want to do a Pete Rose belly-flop, head-first slide into first base that this is the source of your p
Electronics Forum | Mon Jul 26 18:28:10 EDT 1999 | Jon Prokop
Can anyone give me the virtues of SMT package castellations vs. no castellations with particular reference to the ruggedness and reliability of the solder joints? Any references or studies that you can point me to? Also, although I'm in favor of pr
Electronics Forum | Mon Oct 22 11:47:59 EDT 2007 | brulal1
Thank you guys for your help, I do not clean any on my assemblies who are build by the SMT an wave soldering department, we do used liquid fluxes Kester 951 and cored wire keester 245, usually it�s for batteries connector, led, terminal and wire rap