Electronics Forum | Thu Sep 06 10:58:54 EDT 2001 | Steve
If I had to deal with this problem, I would switch to water soluble paste. It is a much more cost effective solution.
Electronics Forum | Fri Sep 07 21:43:40 EDT 2001 | mugen
Hi, We use IPA and Prozone, if IPA is so drastically detrimental, to the pcba's.....what suggested alternative, can you please recommend, as IPA replacement? Thanks.
Electronics Forum | Sun Sep 27 23:10:19 EDT 2009 | hallwayit
Hi, Walter, Why don't you try no-clean flux? We ever met the same condition, later, we changed to no-clean flux solved the problem.
Electronics Forum | Wed Sep 05 14:53:45 EDT 2001 | Jeff Meier
We have customers that are requiring no flux residue left on boards after soldering of non-water washable parts. We currently use Multicore Crystal 502 No-Clean to solder parts that are not washable. Has anyone come up with a good way to remove this
Electronics Forum | Thu Sep 03 11:20:41 EDT 2009 | thunderdog5000
I have a customer that is having a flux residue problem after wave soldering. Flux is roaring through the board to the top side and leaving a residue. This is only happening on the flat stamped leads. The round leads are fine. They are using Supe
Electronics Forum | Thu Sep 06 09:49:26 EDT 2001 | ksfacinelli
This is a real problem. We have experimented with a number of off the shelf products as well as discussed the issue with a few solder manufacturers. As you are aware IPA or Flux off can make the product look worse. I would discuss with the custome
Electronics Forum | Fri Jun 01 16:22:35 EDT 2001 | davef
Your supplier�s approach to managing process change is TOTALLY UNACCEPTABLE!!!! Now, let me get the froth back in my mouth. How in the world do we know if the residues on these "no-clean" boards are compatible with your product? J-STD-001C, para 4
Electronics Forum | Thu Sep 06 10:55:37 EDT 2001 | davef
saturation occurs at ppm levels. Remember, IPA is extremely flammable and its bulk use makes the plant liable to all sorts of quite repressive safety rules/regulations and so on. Ignoring these rules exposes the owner to fines and possible plant cl
Electronics Forum | Thu Sep 06 10:34:21 EDT 2001 | Mike Konrad
Hi Jeff, Sean is correct. Although ultrasonic technology will work in post-reflow de-fluxing applications, you will receive concerns regarding ultrasonic �damage� to wire bonded components. Much has been written to combat this belief but the conce
Electronics Forum | Tue Aug 30 10:46:27 EDT 2005 | lyrtech
Hi, I curently have an interesting challenge. But I don't have all the knowledge to solve it. One of our boards is used in RF applications. We noticed that the No-Clean flux residue makes interferences in the RF signal. Removing the flux residue so