Electronics Forum | Thu Mar 22 16:35:06 EST 2001 | Steve
Deja vu! When I read your response I turned around to see if you standing behind me listening to our problem. We currently make about 50 different boards all using no-clean that have no problems, yet this newest boards has a couple of issues that eng
Electronics Forum | Tue Apr 13 14:56:51 EDT 2004 | russ
in a thread titled ".5mm bga" there is a reference to a paste by alpha that is no-clean and is supposed to be made specifically for this situation. I suppose that increasing the pad dimension to .012" is out of the question? Russ
Electronics Forum | Fri Dec 17 14:13:18 EST 2004 | Claude_Couture
I have done this several times in order to save my butt: adding liquid flux in a jar of not so fresh paste, stirring it slow for 2-3 minutes, to make it usable. Of course, use no-clean flux for no clean paste, etc. During one production slow-down,
Electronics Forum | Wed Mar 21 21:28:22 EST 2001 | davef
We have RF boards with ... * No solder mask * Strategically placed globs of solder It's possible that your boards will not work with NC flux res on them. We generally don't see noise problems. We loose one of the edges [front I think, but don't
Electronics Forum | Thu Mar 22 17:37:06 EST 2001 | davef
Hey!!! Watch it!!! I don�t want to get you believing too much of this stuff. But if you bought that, listen to this � some circuits are so critical with that skin effect stuff that they use silver as the top level solderability preservative. Turn
Electronics Forum | Thu Mar 22 14:12:09 EST 2001 | slthomas
Interesting...the very reason we use water soluble paste on some of our boards is for that reason, although I've never been able to get anyone to show me something in print that supports it. It's just what engineering has told me. We currently have
Electronics Forum | Thu Mar 22 17:38:44 EST 2001 | davef
OK, lemme take a different angle on this, �cuz I forgot to touch on this when I first responded. I mentioned a study ["Evaluation of Low Residue Soldering for Military and Commercial Applications: A Report from the Low-Residue Soldering Task Force"
Electronics Forum | Wed Feb 20 12:47:53 EST 2019 | ccouture
https://murraypercival.wordpress.com/2014/04/08/enclosed-pump-heads-for-stencil-printing/
Electronics Forum | Tue Jan 07 23:38:08 EST 2014 | m_imtiaz
want to know the tolerance the paste height in the solder paste printing. for example if stencil thickness is 7 mil, what will the acceptance level of paste height ( upper and lower) kindly share if any guidelines or formula for the same
Electronics Forum | Thu Jan 30 01:38:22 EST 2014 | m_imtiaz
thank for good input, any documented standard available from any well known body (IPC standard)