Electronics Forum | Thu Aug 07 23:18:27 EDT 2014 | madhuranatha
Sir I more information i did not shared with you. The finish of this critical board is ENIG. Do you recommend ENIG finish for the flight critical boards
Electronics Forum | Mon Aug 04 23:25:28 EDT 2014 | madhuranatha
Let me thank you for the reply. We are manufacturing products which are fitted on the aircraft. We are using SN63Pb37 solder paste for PCB assembly. Of late one of the solder paste supplier recommended SnPbAg for better solder-ability & reliabi
Electronics Forum | Mon Aug 04 23:27:05 EDT 2014 | madhuranatha
Let me thank you for the reply. We are manufacturing products which are fitted on the aircraft. We are using SN63Pb37 solder paste for PCB assembly. Of late one of the solder paste supplier recommended SnPbAg for better solder-ability & reliabi
Electronics Forum | Wed Aug 13 16:43:29 EDT 2014 | anvil1021
This is the perfect combination for the Mission Critical PCBs you require. All of our Airborne Customer Prefer a Leaded Solder to a Lead Free, and often require it. ENIG PCB construction is the strongest method of producing Mission Critical Systems.
Electronics Forum | Fri Jan 28 01:56:32 EST 2005 | Chua
Hi, I could like to find out what are the things need to look out if I'm doing a new SMT solder paste ( water soluble & no-clean ) evaluation. And also flux ( spray type ) for wave-solder ( water soluble & no-clean ). Appreciate for all the input..
Electronics Forum | Wed Aug 06 14:49:06 EDT 2014 | dyoungquist
Sn62Pb36Ag2 has a higher liquidus point of 189C as compared to Sn63Pb37 at 183C. You may need to slightly adjust your oven profiles to use it compared to SnPb. We have had good solder-ability and reliability with it in our IPC Class II products. A
Electronics Forum | Thu Jul 20 13:08:35 EDT 2000 | Bob Willis
The solder paste formulation is different 63/37 is a tin lead alloy so t here is one difference from a lead free. Yes you can get no clean lead free products but if you compare the amount of visible residues they will be normally higher. So far most
Electronics Forum | Tue Jul 16 12:24:25 EDT 2019 | slthomas
In VERY general terms, water soluble flux is usually better at getting good wetting of the soldered connections unless you have a very well controlled process, in which case no-clean can be very handy (you don't have to clean). Water soluble flux re
Electronics Forum | Wed Mar 10 09:52:22 EST 1999 | justin medernach
| We are starting up an SMT line with a printer and convection oven.... The area we are considering for the printer is totally uncontrolled for humidity, temperature and even cleanliness. | | We are working on the filters to keep particulates down,
Electronics Forum | Sat Jun 23 12:42:20 EDT 2001 | genny
OK, to reopen this and muddy the water a little more, What is the difference between REL0 and ROL0 solder. The solder paste that more than one of our suppliers is using is AIM293+ - this is REL0 The no-clean solder wire we use in house is ROL0, mad