Electronics Forum | Wed Jan 17 09:32:09 EST 2007 | Jeff
Hi, I am having problems reworking a lead free PBGA (23mm x 23mm, 1mm pitch). The board is relatively small (5" X 4" X 0.063"). During the removal stage, a thermocouple was placed at the solder ball level (between the board and underneath of compo
Electronics Forum | Tue Dec 30 09:31:52 EST 2014 | rgduval
I've always approached it like this: Design your processes and perform your work to class three standards, and inspect to the standard that is acceptable. That is, all work should be performed to the highest degree of quality. When the work is ins
Electronics Forum | Tue May 27 19:21:50 EDT 2003 | bayanbaru
Can I then say that in general boards are not encourage to rework more than 3 times since the boards will be subjected to Top and Bottom reflow? What is 55110?
Electronics Forum | Tue May 27 10:34:30 EDT 2003 | davef
Much of the ability to survive rework or thermal excursions is dependent upon the fabrication materials. The board qualification criteria under the 55110 was designed around 5 thermal heat cycles. Consider reworking a BGA in this context. BGA i
Electronics Forum | Tue Oct 12 09:52:18 EDT 2010 | dyoungquist
Obviously a totally clean floor is the best. So what if you have 1 particle of dust on your entire production floor? Is that 1 part per million (1 PPM)? or is that 1 part per billion? or 1 part per ???? How do you measure dust and come up with a
Electronics Forum | Sat Feb 24 14:22:53 EST 2001 | johnthor
Well, here I am working Saturday. Seems my production Supervisor had the nerve to get sick on an overtime weekend and, for some peculiar reason, the execs expect the numbers to be met anyway. Go figure! Let me backtrack and clarify that it was th
Electronics Forum | Mon Jun 07 10:57:31 EDT 1999 | Dave F
| | | | Where I can find some informations about repairing of SMT boards? | | | | | | | | Thanks | | | | | | | | Marcos | | | | | | | A first place to start is IPC's 7711 and 7721 encompasing repair, modification, and rework procedures. | | | |
Electronics Forum | Wed Apr 21 00:35:31 EDT 1999 | Scott Cook
| Netters, | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | 1. Kester 293 no clean | 2. 2.1 C/s for 30s to 150 C | 3. .5 - .7 C/s for 60s to 185
Electronics Forum | Mon Jan 04 18:56:25 EST 1999 | Marc P.
| We have a Vitronics SMR400N oven and many times need to use N2 inerting. My problem is that it takes close to an hour of operation to purge the system to achieve the desired O2 levels (~40PPM). This is not only time consuming but results in an inor
Electronics Forum | Thu Mar 09 16:56:19 EST 2000 | Dave F
Ashok: If I was to count, I'd guess there was more than 4 subquestions. Hey, but who's countin' anyway? I have answer (s) "on ESD all related to use of wood in a typical PCB Assembly line:" Before pushing-on, it is only "a typical PCB Assembly li