Electronics Forum | Wed Oct 11 09:55:10 EDT 2000 | Ian Harrison
Some boards that are populated by one of our subcontractors are getting a white powdery residue forming on them. I think it is the non clean flux and process which they are using that is causing the problem. Their process is as follows. Flux is put i
Electronics Forum | Mon Dec 10 13:56:51 EST 2001 | slthomas
1) The additional activity of the OA flux probably took care of the oxydation. How do you plan on taking care of the presence of conductive and corrosive residues from it now, though? You're not supposed to wash those parts with water. 2) The tomb
Electronics Forum | Fri Aug 20 17:17:14 EDT 1999 | K.T
| | | | Yesterday as I was creating a profile on a plastic BGA using Conceptronics freedom 2000 rework station, I happend to discover that I was able to remove solder bridging from a plastic BGA. | | | | | | | | This is what I did. | | | | | | | |
Electronics Forum | Fri Aug 20 14:51:47 EDT 1999 | Tony
| | | Yesterday as I was creating a profile on a plastic BGA using Conceptronics freedom 2000 rework station, I happend to discover that I was able to remove solder bridging from a plastic BGA. | | | | | | This is what I did. | | | | | | Created a
Electronics Forum | Fri Aug 20 14:51:55 EDT 1999 | Tony
| | | Yesterday as I was creating a profile on a plastic BGA using Conceptronics freedom 2000 rework station, I happend to discover that I was able to remove solder bridging from a plastic BGA. | | | | | | This is what I did. | | | | | | Created a
Electronics Forum | Sun Aug 29 19:17:34 EDT 2004 | aqueous
Chen, It is always best to place one�s effort on determining the cause and content of the residue rather than trying to work around it. The first thing you must determine is the nature of the residue. Is it flux? In many instances, the residue is
Electronics Forum | Fri Oct 13 05:21:08 EDT 2000 | Robert Steltman
Looking at the original post, it seems that the white residue is formed on the board after wave soldering and becomes evident when it has been left standing for a while. From what I understand, it seems that the solids content of the "no clean" flux
Electronics Forum | Thu Oct 18 11:20:21 EDT 2001 | davef
Ooooo, you do have the toys, baybeee!!!! This really is not a good situation. * Leaving this OA flux res on your boards will surely affect the LT performance of your product. * That a rookie found this by noticing solder balls all over the seconda
Electronics Forum | Fri Mar 06 10:32:34 EST 2009 | fountain42
Yes, We've already experienced this same problem. 1) What kind of flux are you using? No Clean? Rosin? OA? 2) If it's OA, What kind of water wash do you do? Do you use DI water? How Hot? Who's machine? What are the pressures? 3) Have you performed a
Electronics Forum | Thu Jan 28 14:10:57 EST 1999 | Tom B
Hello Netters, I need some info, Earl or Dave, I have a PCB that exhibits a white layer on solder side. It does not appear to be surface residues (IPA has no effect), but looks like its under solder mask. My first guess is that the LPI solder mask