Electronics Forum | Mon Jan 11 14:48:44 EST 2010 | davef
SR1000 is commonly used for tenting. Search the fine SMTnet Archives on : tenting Someone gave us this note. We have lost their name. It seems to be good advice. If Liquid Photo Image (LPI) solder mask is required, do not tent via holes. Tenting
Electronics Forum | Sun Feb 13 01:35:55 EST 2000 | Dean
Without further information my first guess would be lack of flux to "cut through" the ENTEK layer. Question: In X-ray is the suspect ball of equal diameter when compared to adjacent balls? If no then the volume of solder is different which would po
Electronics Forum | Tue Sep 07 12:45:47 EDT 1999 | Brad Kendall
| Could someone shares their experience on the causes of 'Open' in the BGA after reflow. | | Are you having a problem with the joint openning up after reflow. Like it was soldered after the reflow process, but at final test is not? I had this pr
Electronics Forum | Fri Nov 03 02:32:56 EST 2006 | shivam
HI ALL, can anybody clear me what is via tenting and via pluging?? second one, if i use via in pad for an.5mm bga what care i should taken, what should be the soldermask open in top and innerlayers for via?how it will directly connect to top layer
Electronics Forum | Mon Feb 26 20:02:42 EST 2001 | davef
First, I don�t understand why your board fabricator can�t do a good job plugging your vias. Additionally, when you consider that they forgot to plug the first batch of boards, it makes me wonder if they are desirable as a supplier. Generally, we us
Electronics Forum | Sat Oct 12 06:43:49 EDT 2002 | davef
Alternatives to consider are: * Opening-up your stencil aperture put-down more paste to compensate for the amount that is being used to fill the via. * Relaying-out the board to plug and plate over the via. * Relaying-out the board to move the via fr
Electronics Forum | Wed May 19 11:50:32 EDT 1999 | Chris Nuttall
We care currently running into problems during our plug via process: At the moment we plug prior to soldermask (LPISM) using epoxy resin - plugging takes place from the component side - however we are seeing solderballs after solder level.This is cau
Electronics Forum | Wed May 19 13:13:20 EDT 1999 | Dave F
| We care currently running into problems during our plug via process: | At the moment we plug prior to soldermask (LPISM) using epoxy resin - plugging takes place from the component side - however we are seeing solderballs after solder level.This is
Electronics Forum | Thu May 20 07:53:55 EDT 1999 | Chris Nuttall
| | We care currently running into problems during our plug via process: | | At the moment we plug prior to soldermask (LPISM) using epoxy resin - plugging takes place from the component side - however we are seeing solderballs after solder level.Thi
Electronics Forum | Wed Jan 17 20:48:14 EST 2001 | davef
We find that the raw BGA's pad sheared surface has the SnPb solder at various Z heights whereas the assembled BGAs pad leave a smooth layer of SnPb along the pad. Like to understand the cause for the difference. Who could guess? Solder joint streng