Electronics Forum | Mon Feb 05 20:33:14 EST 2001 | davef
Could you be trying to find: Stevens Products 128 N. Park St E Orange, NJ 07019 973.672.2140 Ross Stevens? Dynamic Technologies (titanium cover w/ silicone jacket, pricey) Stevens makes a U-shaped strip of fiber-material that slips over gold fing
Electronics Forum | Wed Jul 02 03:24:35 EDT 2003 | ramanandkini
did you check with lackwere peters? My frined told me that they have some coatings for this application.
Electronics Forum | Mon Aug 02 11:21:29 EDT 2004 | sforman1
Use MicroCoat Technologies UV cure solder mask. will leave PCB absolutely clean. used in many PCB solder/wirebonding apps. http://www.m-coat.com
Electronics Forum | Mon Jan 25 21:43:04 EST 1999 | Dave F
| hi, | i am working towards developing a no-clean process for a customer at contract manufacturing facility. the assemblies have gold fingers on them. these are masked to prevent from any damage to them during reflow soldering. the earlier proces
Electronics Forum | Sun Jan 31 23:03:57 EST 1999 | Dennis O.
| | hi, | | i am working towards developing a no-clean process for a customer at contract manufacturing facility. the assemblies have gold fingers on them. these are masked to prevent from any damage to them during reflow soldering. the earlier pr
Electronics Forum | Wed Feb 03 18:36:47 EST 1999 | Earl Moon
| Does anyone know if I will have problems soldering surface mount components to an all hard gold plated PC board. We want to use hard gold similar to gold used for edge fingers because our customer is concerned about wear and conductivity of connect
Electronics Forum | Fri Sep 06 14:03:18 EDT 2013 | horchak
If you are a CEM you are setting yourself up for failure and will be left holding the bag. Flash gold has one purpose. It is a protective coating for the base medal to keep it from oxidizing. It is very thin and will be absorbed into the solder joint
Electronics Forum | Sun Dec 31 07:31:40 EST 2006 | davef
Thoughts are: * Eliminate solder spotting on gold fingers through process improvement in broard handling, printing paste control, and reflow recipe development. Search the fine SMTnet Archives for previous discussions. * Dispense or print a reflow te
Electronics Forum | Thu Aug 25 17:24:44 EDT 2016 | davef
Gold should not be corroding in salt water. I have swum hundreds of miles in salt water with my wedding ring on my finger. My ring is a shiny and corrosion-free as the day it was cast over 120 years ago. It's possible that your gold thickness of 0.0
Electronics Forum | Fri Jul 02 09:54:02 EDT 1999 | John Thorup
| | | | We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design)