Electronics Forum | Wed Jun 23 13:34:29 EDT 2004 | df_indy
I am four weeks into my new job, there always seems to be some issues here with PCB every week. Today while I was checking some assemblies with micro-scope, I found a lot of tiny bubbles/blisters on the board. They are just little dots if you look
Electronics Forum | Mon Jan 25 21:43:04 EST 1999 | Dave F
| hi, | i am working towards developing a no-clean process for a customer at contract manufacturing facility. the assemblies have gold fingers on them. these are masked to prevent from any damage to them during reflow soldering. the earlier proces
Electronics Forum | Sun Jan 31 23:03:57 EST 1999 | Dennis O.
| | hi, | | i am working towards developing a no-clean process for a customer at contract manufacturing facility. the assemblies have gold fingers on them. these are masked to prevent from any damage to them during reflow soldering. the earlier pr
Electronics Forum | Fri Jul 02 09:54:02 EDT 1999 | John Thorup
| | | | We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design)
Electronics Forum | Sun Nov 01 23:51:44 EST 2009 | boardhouse
Hi Julie, My opinion is that the top board would not pass IPC, solder mask encroachment on pads. Second board is what we call Orange peel,this can be caused two way's. 1) the solder mask was not tack dried enough prior to imaging which caused artwo
Electronics Forum | Thu Jan 24 09:53:56 EST 2002 | davef
You didn�t tell us about your solder, wave temperature profile, or the distribution of the problem. So, let�s assume the solder is near eutectic and the problem is wide spread. Wolfgang makes good points. So, let's talk a different tact. When we
Electronics Forum | Wed Sep 01 14:15:27 EDT 1999 | Dave F
| Help | | I have just received some PCBs with external tracks entering SMD pads at all angles, tangents + 45 degs etc. | | Where can I obtain information as to how tracks should enter SMD pads.? I have looked at several IPC books and got some mino
Electronics Forum | Fri May 26 04:58:19 EDT 2023 | auriga2001
I agree with the two other replies. Left alone, it is a defect. If it's just excess adhesive or coating, you can use IPC-7711/7721 'Rework, Modification and Repair of Electronic Assemblies' for guidance on removing. Section 2.3.1 explains how to te
Electronics Forum | Mon Oct 11 11:13:32 EDT 1999 | Wirat S.
| | | We've recently encountered this problem where one of our .050" pitch BGA's were reflowing at the wave thus causing shorts... The board was profiled with probes stuck to a QFP solder joint, an 0603, and one of the BGA joints. There was an almo
Electronics Forum | Fri Jan 15 15:06:30 EST 1999 | Earl Moon
| Hello, | | We are qualifying new sources of PWB vendors. We've got the first lot of "produciton" boards in and we want to put them through the paces before turing the vendors on. | | So far, the tests I can think of performing, and that we have