Electronics Forum | Fri Aug 28 13:23:50 EDT 1998 | Ben Salisbury
| | | | | Damn Wayne, | | | | | | If I knew as much as you, Justin, Steve, his dad, and others know, or knew, I'd be happy to be the UGLY. The plus of a forum like this is it keeps us on our toes and keeps our brain cells alive or constantly searchin
Electronics Forum | Mon Jul 27 17:38:55 EDT 1998 | Steve Gregory
Hi Stoney, Justin is giving you some good advice, unfortunately these kinda' problems sometimes call for the ol' D.O.E...otherwise, you could be chasing your tail for a while until you figure out exactly what's causing your problems. Has the ep
Electronics Forum | Tue Jul 28 17:35:07 EDT 1998 | Brian Stumm
Steve, I know it is tempting to go for the cheapest method of applying conformal coatings but I must warn you. If you are a contract manufacturer then you don't want to limit yourself in the types of coatings you can work with. Just as soon as you se
Electronics Forum | Tue Jul 28 17:44:03 EDT 1998 | Brian Stumm
| Steve, | I know it is tempting to go for the cheapest method of applying conformal coatings but I must warn you. If you are a contract manufacturer then you don't want to limit yourself in the types of coatings you can work with. Just as soon as yo
Electronics Forum | Fri Jul 24 06:50:58 EDT 1998 | Wayne
| Hey youse guyz... | We're finally getting our first real job at the start-up I'm working at. It's actually a pretty unique little board too. Simple as all get out, but unique. You're not gonna believe what this goes into...guess? (I bet ya' you'll
Electronics Forum | Fri Jul 24 13:41:05 EDT 1998 | Bob Willis
Sorry guys have a look at this list of component weights and then work out the surface area of the lead/pad and then come back on the PLCC issue. Chip 0805���� 0.007g������ 2 Chip 1206���� 0.009g���� 2 Chip 1210���� 0.012g���� 2 SOT23���������0.008g�
Electronics Forum | Thu Jul 02 15:23:15 EDT 1998 | Justin Medernach
| | I'm having a problem getting good reflow on gold sufaced boards. The profile looks good and I have adjusted it both hotter and colder and adjusted the various times ( soak, reflow ) to no avail. What realy gets me Is that a month ago we built som
Electronics Forum | Fri Jun 12 10:18:50 EDT 1998 | smd
| | | | In our continued search for another flex machine, we reconsidered Philips | | | Emerald (low Vol/high mix Mfg). We already have a CSM so it makes a little sense. Then the salesman started talking about the Topaz. The Topaz supposedly is "pra
Electronics Forum | Wed Jun 03 21:25:33 EDT 1998 | John Allan
| Hello: | BACKGROUD: SMT components soldered on the top-side of boards that also require wave soldering have the potential to reflow during wave soldering. Reflowing these components during wave soldering is not good. It can cause cold joints, op
Electronics Forum | Thu Jun 04 08:32:21 EDT 1998 | Dave F
| | Hello: | | BACKGROUD: SMT components soldered on the top-side of boards that also require wave soldering have the potential to reflow during wave soldering. Reflowing these components during wave soldering is not good. It can cause cold joints