Electronics Forum | Thu Feb 07 12:50:21 EST 2019 | gregcr
Hi All, What are you running for selective solder flux? I'd like any opinion on water soluble and/or no-clean fluxes you are using. In our Kiss 104 machine we use HYDRO-X20 water soluble flux, per the original install suggestion, but I'd like to k
Electronics Forum | Fri Feb 08 10:52:24 EST 2019 | roblackey
BLT 31-41 "No Clean Selective Flux For Aerospace" On a Versaflow 3/45 Atomises well, good hole penetration, good wetting, cleans off well in the solvent cleaner. Use for SN100C, SA0307, and 60/40.
Electronics Forum | Wed Feb 13 13:30:03 EST 2019 | emeto
I personally prefer a NC process if I have to chose. AIM flux was good NC377 I think(they keep changing names), NF 372 from and many more. You can make them all work...the KISS 104 ...
Electronics Forum | Fri Mar 22 14:19:38 EDT 2019 | gregcr
Thank you ProcEng1 Nordson sent me a flux suggestion list: No Clean: 1. Kester Select 10 2. ALPHA EF-2210 3. AIM FX-16 Water Sol: KESTER 2331-ZX Nozzle Tinning: SUPERIOR #75
Electronics Forum | Tue Feb 29 10:14:02 EST 2000 | Robert Hartmann
My company is just getting into the flip chip packaging arena. We are putting in a prototype/small volume wire bond PBGA line. We have some questions with regard to choosing solder balls and cleaning of flux. 1) Is there a formula for the shrink
Electronics Forum | Tue Feb 29 10:14:02 EST 2000 | Robert Hartmann
My company is just getting into the flip chip packaging arena. We are putting in a prototype/small volume wire bond PBGA line. We have some questions with regard to choosing solder balls and cleaning of flux. 1) Is there a formula for the shrink
Electronics Forum | Fri Mar 22 14:07:00 EDT 2019 | proceng1
I believe that NORDSON now recommends AIM NC277. Nordson bought out ACE-protech.
Electronics Forum | Fri Oct 10 05:04:26 EDT 2008 | bing007
We are using Mulicore MF101 flux and a Vitronics selective soldering machine on a lead-fee assembly and are having trouble with nozzles blocking even when the nozzle aperture is increased. Has anyone come across this problem before using fluxes with
Electronics Forum | Tue Oct 14 17:45:20 EDT 2008 | gregoryyork
is that the milky emulsion one ???
Electronics Forum | Wed Mar 01 16:59:44 EST 2000 | Dave F
Robert: Expect a 0.033" raw ball to be within 0.022" of the pad, after reflow. To be clear, that�s not a matter of shrinking by 33%. The volume of solder on the pad is the same as the volume of solder in the raw ball. It�s just that the solder is