Electronics Forum | Wed Nov 24 16:08:09 EST 2004 | Terrapin Station
This depends on the model. Most machines and turret style typically overstroke .2mm with a force of 250 - 300 grams of force. the reason for the over stroke is to place the component into the paste. This can be adjusted through part library manipul
Electronics Forum | Wed Dec 15 15:51:42 EST 1999 | cb
Tracy, Gary made some good points, you could also to check to see if you have the printer taking a long enough stroke over the board. I have seen some people not have the squeege come across the board enough and the paste roll is still setting over
Electronics Forum | Tue Sep 18 13:58:01 EDT 2001 | ert002
50%) only over the appertures where there was poor support. Most prints took 2 knead strokes to print OK, but this caused fine pitch leaded devices to almost short. stencil had to be be wiped after kneading. 2 similar devices with exactly the same
Electronics Forum | Sun Mar 26 19:02:05 EST 2006 | ms
Hi We are running automatic stencil printers, open squeegees, stainless stencil, stainless blades, print speed 25-30mm/sec. We have a frustrating consistency issue printing .37x.3mm apertures on a 45pin LGA (11 pads each side, 1 large ground in mid
Electronics Forum | Fri Mar 29 10:11:02 EDT 2019 | cyber_wolf
“For a number of years now, work has been proceeding in order to bring perfection to the crudely conceived idea of a transmission that would not only supply inverse reactive current for use in unilateral phase detractors, but would also be capable of
Electronics Forum | Sat Nov 15 05:08:45 EST 2014 | grimus
Same side (component side) if You give me e-mail I can provide You more pictures. I'm making one stroke with same speed (I'm using closed proflow head and DEK printer). 5 mils thickness stencil. Products requirement - 3 IPC Class (75 % and more fill
Electronics Forum | Thu Aug 12 22:38:44 EDT 1999 | Dave F
| Hello | | Having a problem with bridging on 20mil pitch qfp, only on the lead groups where squeegee goes over width of apertures. Using MPM sp-200 semi-auto, chem-etch stencil, 9-10mil width opening | 100 durometer blade. Getting "tails" on deposi
Electronics Forum | Tue Nov 20 20:56:23 EST 2001 | davef
You�re correct. The release characteristics of epoxy differ from solder paste. Consider: * Using print/flood stroke, on-contact print cycle. * Printing slow enough to fill the hole with adhesive. * Overcoming the thixotropic [The viscosity of thixo
Electronics Forum | Thu Jun 24 07:22:19 EDT 2004 | cyber_wolf
I know I have posed this question before, but I would like to open this discussion again. We do several change overs through the course of three shifts on our CP642 line. When we start a new job, we have tons of tape feeder overlay problems.(The over
Electronics Forum | Mon Jun 02 19:52:03 EDT 2008 | operator
So what happens in this hypothetical model when the customer provides you all the data you asked for and then your programmer finds out that it is the wrong revision data or the BOM is truncated or the centroids are missing refs, etc... Then new data