Electronics Forum | Thu Jun 09 14:45:21 EDT 2011 | kahrpr
Does the board look like that before Reflow?
Electronics Forum | Fri Jun 17 13:51:21 EDT 2011 | mosborne1
Your problem is at your board house with the finish. There is not enough tin deposited on the ground plane. Could be the current density too low on the ground plane. If electroless they just didn't process these correctly. What is the finish suppose
Electronics Forum | Wed Jun 08 13:49:48 EDT 2011 | sonofptolemy
Hello, I am having a problem with HASL PCB's after it comes back from the stuffer. To me it looks like oxidation and it causes poor wetting. This leads to a bunch of problems all of which have different symptoms but the cause is this oxidation proble
Electronics Forum | Thu Jun 16 17:02:40 EDT 2011 | boardhouse
The finish looks like Immersion Tin or Silver. if its lead free Hot air - could be issue of to high of a Tin Content. find out what brand of Hasl they are using. SL100 Example. Is this tarnished look only being seen after assembly or have you seen
Electronics Forum | Wed Apr 23 19:00:39 EDT 2008 | stevek
It depends on the laminate but a PWB is like any other MSL component. Some fab shops are only waranting standard FR4 laminates for 45-60 days when processed at lead free temperatures. The best thing I can say is to try some weight gain/loss experim
Electronics Forum | Tue May 15 21:57:06 EDT 2001 | davef
Welcome!!! Where the hay ya been??? Sorry bud, were lining-up with your fab [it hurts me to say that, but when yer ] We used to dry pack with desiccants, also. Its probably an old MIL-STD-2073-1C requirement [er something like that]. We qui
Electronics Forum | Wed May 16 08:48:12 EDT 2001 | ohboy
I been a bunch o' places...! Some good, some bad, re-inventing the wheel in many cases. Our specs are pretty specific in a lot of cases, but that doesn't mean they always get followed. It usually becomes a case of "It's not quite right, but we rea
Electronics Forum | Tue Apr 26 11:22:48 EDT 2005 | denismeloche
I have found that Sn62 solder gives better strength and leach resistance when soldering to gold surfaces. The gold needs to be at least 5 to 10 micro inches thick to prevent nickel oxidation but if over 25 micro inches will cause brittleness. I hav
Electronics Forum | Sun Mar 07 08:33:37 EST 2010 | joseph_smile
HI GET ME INFO ABT PCB OXIDIZATION WITH REGARDS JOSEPH
Electronics Forum | Fri Aug 08 23:31:45 EDT 2008 | hanward
Hello,man,we are a PCB manufacturer.I can ask our engineer and reply you.
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830
.gif)
winsouce.jpg)