Electronics Forum | Wed Feb 22 21:21:09 EST 2023 | cbeneat
One expense reduction is to order parts from SMTXTRA. I am not affiliated at all with them; however, I buy from them as much as possible. Usually 30-40% price difference from Panasonic. Example is the waste bins for Panasonic NPM's-$183.49, Last time
Electronics Forum | Mon Apr 28 16:36:11 EDT 2003 | razor
Component: Termination (barrier) NI, 120/3.0 um Solder Plate (outer) 90% Sn, 10% Pb, 120/3.0 um Solder: Multicore CR39, 95.5%Sn/3.8%Ag/.7%Cu @ 6mil Flex PCB: Cu, Ni, Au .2m to .5m Thanks
Electronics Forum | Thu Oct 04 00:03:28 EDT 2018 | gaintstar
flason smt pick and place machine: http://www.flason-smt.com/product/Hanwha-IC-placer-SM321-High-Speed-SMT-Modular-Chip-Mounter.html http://www.flason-smt.com/product/Hanwha-Pick-and-Place-Machine-DECAN-F2-High-Speed-SMT-Modular-Chip-Mounter.html htt
Electronics Forum | Wed Aug 10 21:47:17 EDT 2005 | Geoff
Nihon superior could not provide any written aprovals but In asia.......... Sony- SN100C in use for car and home audio applications. Panasonic- SN100C in use for DVD, VCR, battery, and home appliances applications. Pioneer- SN100C in use for everythi
Electronics Forum | Sat Oct 01 01:25:30 EDT 2005 | ck
Sorry theres a mistake on previous question. It should be lead free component termination but non lead free solder alloy Sn63/Pb37. The reflow profile i am using : Soaking temp. 120 to 160 deg C; time 90 to 120 sec. Peak temp. 215 to 225 deg C; time
Electronics Forum | Wed Oct 04 15:06:57 EDT 2006 | C.K. the Flip
Hmmm.. you are in a pickle then. I have AIM's "Reflow Profile Supplement" where they recommend a Low-Long-Soak (LSS) profile for situations like your's. It's an old-school type profiling approach where you ramp up to 120*C for about 1 min. then soa
Electronics Forum | Wed Jun 29 03:37:53 EDT 2005 | lupo
Hi, I think that the time depends on the type of stainless steel, temperature and solder alloy. For example, one of our machines is delivered with 316 stainless pot and alloy SnNi. It worked six months (120days*16hours = 1920hours) and aft
Electronics Forum | Fri Jan 20 09:17:59 EST 2006 | George
Hi "theSaint", We are using SN100C in our wave solder machine. As far as the solder itself, the wave process follows pretty much the same concept as leaded solder. You bring the assembly temp to 90 C or more before the actual wave. Sometimes for mul
Electronics Forum | Fri Sep 23 13:43:42 EDT 2022 | klauss
Hi, How do we know what values we should use to add new nozzles into library? There are VU, VD, TT, MT, FB, Adhesion Check and SN blanks but i am not sure what they should be. Is there any default settings for them?
Electronics Forum | Tue Aug 10 15:42:20 EDT 2010 | flipit
I had 2 Contact 3AV and 2 Contact 3Z machines. Basically the same as 3AVX machines. Both models are good machines. They are perfect for small production and even medium production size lots if you have multiple machines. Super easy to operate and