Electronics Forum | Thu Aug 23 09:52:38 EDT 2007 | d0min0
Hi, in past we had an issue with ENIG surface, black was Ni that get pass the Au - but it was discovered after reflow (SnPb) and the IC was losing contact with Cu tracks...at customers application :| Reason was as I remember too thin Au sufrace... w
Electronics Forum | Tue Aug 21 05:05:52 EDT 2007 | vangogh
Hi All, I would like to get some inputs regarding this.... I have bare PCB which were stored with kapton tape attached on the Au plated pads. These were stored for close to a year. Upon removal of kapton tape, we noticed discolorations on the edges o
Electronics Forum | Wed Aug 22 21:42:54 EDT 2007 | davef
Questions are: * Do these pads take solder? How well? * Have you stripped the gold and evaluated the condition of the nickel?
Electronics Forum | Mon Aug 27 08:03:32 EDT 2007 | davef
Actually, you will be soldering and wire bonding to the palladium layer, so we should have asked if you checked that layer, rather than the nickel. We not sure of the source of the copper that your see on EDX. It's possible copper from the pad migra
Electronics Forum | Sun Aug 26 11:27:12 EDT 2007 | vangogh
Hi Davef, Thanks for the reply. There seem to be no issues on SMT reflow based on some samples done. We have not stripped the gold yet. We did a X-section+EDX and we are seeing traces of copper on the nickel layer. Any idea what is the implication of
Electronics Forum | Thu Aug 30 09:49:32 EDT 2007 | blnorman
EDS @ 10kV maybe going too deep. I've talked to a surface science physicist that recommends Auger spectroscopy because it's more of a true "surface" examination tool.
Electronics Forum | Mon Oct 16 17:46:49 EDT 2006 | Dan
Recently I was given a bad Bios Link from Toshiba which fried my Bios and now my laptop boots to a black screen. I recently unsoldered and removed the existing Bios chip and have ordered anotherfor replacement. Unfortunately while removing, i damag
Electronics Forum | Fri Jun 08 17:22:51 EDT 2007 | naynayno
We have been producing an IMS assembly with SMT dpak's for some time. However, we recently encountered a new problem by chance - the parts can be flicked off with a finger nail. I state by chance because the solder joints are wetted and shiny with
Electronics Forum | Thu Nov 07 15:33:02 EST 2013 | mleber
Below are a few photos of an ongoing issue we are having with 1 pwb style. Some of the pads appear to have contamination that appears after the selective solder step. The joints are extremely hard to rework - almost impossible. We had the joints anal
Electronics Forum | Fri Nov 08 17:49:05 EST 2013 | davef
First, it's a surprise that your failure analysis lab thought everything was OK with these boards. They look like shit. Second, a few years ago, there was a bunch of complaints about ENIG boards with issues similar to what you're observing. There wa
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830
.gif)
winsouce.jpg)