Electronics Forum | Tue Dec 08 17:55:51 EST 1998 | Dave F
1. What is the best way to remove polyurethane conformal coating from selected areas? Your conformal coat material supplier is best equipped to tell you how to remove the coating. Polyurethane conformal coating is not easy to remove. Without in-pu
Electronics Forum | Thu May 07 20:28:35 EDT 2009 | davef
From our notes, the following is a series of snips from: "Copper Dissolution in Tin" LJ Turbini, PhD, adjunct faculty member, University of Toronto, Materials Science and Engineering, SMT 2/07 As the solder becomes molten, copper from the board diff
Electronics Forum | Wed Oct 17 09:38:55 EDT 2001 | fmonette
Dear Daniel, I assume that these components are moisture-sensitive. If they have absorbed too much moisture prior to reflow you might be experiencing popcorning. This typically shows up as a bulge over the surface of the die, in the center of the p
Electronics Forum | Thu Aug 09 09:05:09 EDT 2007 | davef
There are no requirements acceptance criteria for baking of board assemblies. What are your customer requirements? The common reasons people choose to bake PCB are to prevent: * Delamination of multilayer boards * Measles, particularly on double si
Electronics Forum | Sat Jun 13 11:00:21 EDT 1998 | Earl Moon
| We are very concerned about outgassing in wavesoldering. | If anyone knows how to use properly well pcb's before soldering in order to avoid this problem please let me know. I have this problem in FR4 large double sided pcb's. My soldering line is
Electronics Forum | Mon Feb 18 15:47:42 EST 2008 | ck_the_flip
In theory, no clean flux residues are electrically benign...period. Here's a good test. Subject the board to some moisture/humidity, and have your circuit designer ohm-out any areas that may be affected by conductive material. Option B: Have a la
Electronics Forum | Tue Aug 26 07:44:06 EDT 2008 | davef
Industry-wide, there is no current requirement for baking of bare boards. It adds no value. * IPC-HDBK-001 has guidelines olden times. * IPC-TM-650 has several test methods to determine moisture resistance to both liquid immersion and absorption from
Electronics Forum | Tue Dec 09 10:04:36 EST 2008 | lazzara55
SMT-ypw: Does PWB supplier start to implement PWB drying packaging? B3: YES! The fabrication of the PCB involves a series of wet processing that requires counter-measures to remove moisure. While some of the PCB processes also include bake cycles th
Electronics Forum | Thu Jan 28 16:29:03 EST 1999 | Tom B
Okay, Another question, if the soldermask in not cured, then it is washed will water ingress (from wash or ambient ) play havoc with capacitance or dielectric of PCB. I mean will my crystal and clock circuits start "Y2K'n" on me. OR will my PCB go
Electronics Forum | Thu Nov 13 12:08:50 EST 2008 | cisridn
I define First Pass yield without any repairs. But I only consider a PCB to need repair if it fails test. Our boards are inspected before testing and any work done before testing, I consider to be rework and is part of the SMT process.
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830
.png)